Optically isotropic liquid crystal medium and optical device

ABSTRACT

A liquid crystal medium, which has a liquid crystal phase over a wide temperature range, a large refractive index anisotropy, and a large dielectric anisotropy, and exhibits an optically isotropic liquid crystal phase, is provided. The liquid crystal medium is characterized by containing a liquid crystal compound having four benzene rings and a difluoromethyleneoxy group, and a chiral reagent, and exhibiting an optically isotropic liquid crystal phase.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention generally relates to a liquid crystal mediumuseful as a material for an optical device, and in particular, to aliquid crystal medium having a liquid crystal phase over a widetemperature range, and having a large dielectric anisotropy and a largerefractive index anisotropy. The present invention further relates to anoptical device using the liquid crystal medium, and in particular, to anoptical device that can be used in a wide temperature range and drivenat a low voltage, and is capable of achieving a high-speedelectro-optical response. The so-called optical device refers to variousdevices using electro-optic effect to achieve the function of opticalmodulation or optical switching, for example, display devices (LCDdevices) and optical modulation devices used in optical communicationsystems, optical information processing or various sensor systems.

2. Description of Related Art

Liquid crystal display (LCD) devices utilizing liquid crystalcompositions are widely used as the display for clocks, calculators,word processors, and so on. These LCD devices utilize the refractiveindex anisotropy and dielectric anisotropy and the like of liquidcrystal compounds. The operation modes of the LCD devices are known andmainly include phase change (PC), twisted nematic (TN), super twistednematic (STN), bistable twisted nematic (BTN), electrically controlledbirefringence (ECB), optically compensated bend (OCB), in-planeswitching (IPS), and vertical alignment (VA) and so on, which utilizeone or more polarizers for display. Moreover, in recent years, moreattention has been paid to the mode where an electric field is appliedto an optically isotropic liquid crystal phase to induce electricbirefringence (Patent References 1-9, and Non-patent References 1-3).

Moreover, wavelength variable filters, wavefront control devices,liquid-crystal lenses, aberration correction devices, aperture controldevices, and optical head devices and the like that utilize the electricbirefringence in a blue phase as one of the optically isotropic liquidcrystal phases have been proposed (Patent References 10-12).

According to the driving mode, the devices can be classified intopassive matrix (PM) and active matrix (AM) types. The PM type is furtherclassified into static type and multiplex type, and the AM type isfurther classified into thin film transistor (TFT) type andmetal-insulator-metal (MIM) type.

Such LCD devices contain a liquid crystal composition having suitablephysical properties. In order to improve the characteristics of an LCDdevice, the liquid crystal composition preferably has suitable physicalproperties. A liquid crystal compound as a component of the liquidcrystal composition requires to have the following general properties:

(1) stable chemical properties and stable physical properties;

(2) a high clearing point (i.e., phase transition temperature from theliquid crystal phase to the isotropic phase);

(3) a low lower-limit temperature of a liquid crystal phase (i.e.,optically isotropic liquid crystal phase, such as nematic phase,cholesteric phase, smectic phase, and blue phase);

(4) excellent compatibility with other liquid crystal compounds;

(5) a suitable dielectric anisotropy; and

(6) a suitable refractive index anisotropy.

Particularly, for an optically isotropic liquid crystal phase, a liquidcrystal compound having a large dielectric anisotropy and a largerefractive index anisotropy is preferred, in view of lowering thedriving voltage.

When a liquid crystal composition containing a liquid crystal compoundhaving stable chemical and physical properties as described in (1) isused in an LCD device, the voltage holding ratio is improved.

Further, a liquid crystal composition containing a liquid crystalcompound having a high clearing point or a low lower-limit temperatureof a liquid crystal phase as described in (2) and (3), may have anexpanded temperature range of a nematic phase or optically isotropicliquid crystal phase, and thus can be used in a display device in awider temperature range. A liquid crystal composition is generallyprepared by mixing a liquid crystal compound with a number of otherliquid crystal compounds, so as to exhibit better properties that aredifficult to develop by a single liquid crystal compound. Therefore, aliquid crystal compound having good compatibility with other liquidcrystal compounds as described in (4) is preferably used in an LCDdevice. In recent years, LCD devices with superior properties,especially display performance such as contrast, display capacity, andresponse time, are required. In addition, as for the liquid crystalmaterial that is being used, a liquid crystal composition having a lowdriving voltage is required. Furthermore, in order to drive an opticaldevice that is driven in an optically isotropic liquid crystal phasewith a low voltage, a liquid crystal compound with a large dielectricanisotropy and a large refractive index anisotropy is preferred.

As for the optically isotropic polymer/liquid crystal compositematerials disclosed in Patent References 1-3 and Non-patent References1-3, high voltages for device operation are required. Although opticallyisotropic liquid crystal compositions and polymer/liquid crystalcomposite materials, which are expected to have an operation voltagelower than the voltages as described above, are disclosed in PatentReferences 4-9, an optically isotropic liquid crystal composition and apolymer/liquid crystal composite material of the present invention werenot disclosed.

REFERENCES IN PRIOR ART

[Patent References]

[Patent Reference 1] Japanese Patent Publication No. 2003-327966

[Patent Reference 2] International Publication No. 2005/90520 pamphlet

[Patent Reference 3] Japanese Patent Publication No. 2005-336477

[Patent Reference 4] Japanese Patent Publication No. 2006-89622

[Patent Reference 5] Japanese Patent Publication No. 2006-299084

[Patent Reference 6] Japanese Patent Publication No. 2006-506477

[Patent Reference 7] Japanese Patent Publication No. 2006-506515

[Patent Reference 8] International Publication No. 2006/063662 pamphlet

[Patent Reference 9] Japanese Patent Publication No. 2006-225655

[Patent Reference 10] Japanese Patent Publication No. 2005-157109

[Patent Reference 11] International Publication No. 2005/80529 pamphlet

[Patent Reference 12] Japanese Patent Publication No. 2006-127707

[Non-patent References]

[Non-patent Reference 1] Nature Materials, 1, 64, (2002)

[Non-patent Reference 2] Adv. Mater., 17, 96, (2005)

[Non-patent Reference 3] Journal of the SID, 14, 551, (2006)

SUMMARY OF THE INVENTION

The present invention is directed to a liquid crystal medium, which isstable to heat and light, has a liquid crystal phase over a widetemperature range, a large refractive index anisotropy and a largedielectric anisotropy, and exhibits an optically isotropic liquidcrystal phase. The present invention is further directed to variousoptical devices containing the liquid crystal medium, which can be usedover a wide temperature range, and have a short response time, a highcontrast, and a low driving voltage.

The inventors identifies that, in order to have a liquid crystal phaseover a practical temperature range in one aspect and exhibit a largerefractive index anisotropy and dielectric anisotropy in another aspect,a liquid crystal composition having a compound of Formula (1) with fourbenzene rings and at least one linking group —CF₂O— as a main componentand exhibiting an optically isotropic liquid crystal phase is suitable.The present invention provides a liquid crystal medium (liquid crystalcomposition or polymer/liquid crystal composite) and an optical devicecontaining the liquid crystal medium.

[1] A liquid crystal composition, containing an achiral component Tincluding a compound of Formula (1), and a chiral reagent, andexhibiting an optically isotropic liquid crystal phase.

(in Formula (1), R¹ is hydrogen or a C₁₋₂₀ alkyl, wherein arbitrary—CH₂— in the alkyl may be substituted with —O—, —S—, —COO—, —OCO—,—CH═CH—, —CF═CF— or —C≡C—, and arbitrary hydrogen in the alkyl and thealkyl with arbitrary —CH₂— substituted with —O—, —S—, —COO—, —OCO—,—CH═CH—, —CF═CF—, or —C≡C— may be substituted with halogen or a C₁₋₃alkyl; Z¹, Z², and Z³ are each independently a single bond, —COO—, or—CF₂O—, provided that at least one of Z¹, Z², and Z³ is —CF₂O—; and L¹,L², L³, L⁴, and L⁵ are each independently hydrogen or fluorine; X¹ ishydrogen, halogen, —SF₅, or a C₁₋₁₀ alkyl, wherein arbitrary —CH₂— inthe alkyl may be substituted with —O—, —S—, —CH═CH—, or —C≡C—, andarbitrary hydrogen in the alkyl and the alkyl with arbitrary —CH₂—substituted with —O—, —S—, —CH═CH—, or —C≡C— may be substituted withfluorine.)

[2] The liquid crystal composition according to item 1, in which inFormula (1), R¹ is a C₁₋₂₀ alkyl, a C₂₋₂₁ alkenyl, a C₂₋₂₁ alkynyl, aC₁₋₁₉ alkoxy, a C₂₋₂₀ alkenyloxy, a C₁₋₁₉ alkylthio, a C₁₋₁₉alkenylthio, or —(CH₂)v-CH═CF₂, in which v is an integer of 0 or 1-19;and X¹ is hydrogen, halogen, —SF₅, —CH₂F, —CHF₂, —CF₃, —(CH₂)₂—F,—CF₂CH₂F, —CF₂CHF₂, —CH₂CF₃, —CF₂CF₃, —(CH₂)₃—F, —(CF₂)₃—F, —CF₂CHFCF₃,—CHFCF₂CF₃, —(CH₂)₄—F, —(CF₂)₄—F, —(CH₂)₅—F, —(CF₂)₅—F, —OCH₂F, —OCHF₂,—OCF₃, —O—(CH₂)₂—F, —OCF₂CH₂F, —OCF₂CHF₂, —OCH₂CF₃, —O—(CH₂)₃—F,—O—(CF₂)₃—F, —OCF₂CHFCF₃, —OCHFCF₂CF₃, —O—(CH₂)₄—F, —O—(CF₂)₄—F,—O—(CH₂)₅—F, —O—(CF₂)₅—F, —CH═CHF, —CH═CF₂, —CF═CHF, —CH═CHCH₂F,—CH═CHCF₃, —(CH₂)₂—CH═CF₂, —CH₂CH═CHCF₃, or —CH═CHCF₂CF₃.

[3] The liquid crystal composition according to item 1 or 2, in which inFormulas (1), Z¹, Z², and Z³ are each independently a single bond or—CF₂O—.

[4] The liquid crystal composition according to any one of items 1 to 3,in which R¹ is a group of any one of Formulas (CHN-1)-(CHN-19), andR^(1a) is hydrogen or a C₁₋₂₀ alkyl.

[5] The liquid crystal composition according to item 1, containing atleast one compound selected from the group consisting of the compoundsof Formulas (1-1)-(1-3).

(in the formulas, R¹ is a group of any one of Formulas (CHN-1)-(CHN-19),and R^(1a) is hydrogen or a C₁₋₂₀ alkyl; L¹, L², L³, L⁴, and L⁵ are eachindependently hydrogen or fluorine; and X¹ is fluorine, chlorine, —CF₃,—CHF₂, —CH₂F, —OCF₃, —OCHF₂, —OCH₂F, —OCF₂CFHCF₃, or —CH═CHCF₃.)

[6] The liquid crystal composition according to item 5, in which inFormulas (1-1)-(1-3), R¹ is a group of any one of Formulas(CHN-1)-(CHN-4) and Formulas (CHN-6)-(CHN-8), and R^(1a) is hydrogen ora C₁₋₂₀ alkyl.

[7] The liquid crystal composition according to any one of items 1 to 6,in which the achiral component T further contains a compound of Formula(2).

(in Formula (2), R² is a group of any one of Formulas (CHN-1)-(CHN-4)and Formulas (CHN-6)-(CHN-7), R^(1a) is hydrogen or a C₁₋₂₀ alkyl; RingsA¹, A², A³, A⁴, and A⁵ are (RG-1)-(RG-13); Z⁴, Z⁵, Z⁶, Z⁷, Z⁸, and Z⁹are each independently a single bond or a C₁₋₄ alkylene, whereinarbitrary —CH₂— in the alkylene may be substituted with —O—, —COO— or—CF₂O—; L⁶, L⁷ and L⁸ are each independently hydrogen or fluorine; X² isfluorine, chlorine, CF₃, —CHF₂, —CH₂F, —OCF₃, —OCHF₂, —OCH₂F,—OCF₂CFHCF₃, or —CH═CHCF₃; and l, m, n, o, and p are each independently0 or 1, provided that l+m+n+o+p≦4.)

[8] The liquid crystal composition according to item 7, in which inFormula (2), R² is hydrogen or a C₁₋₂₀ alkyl, wherein arbitrary —CH₂— inalkyl may be substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—, —CF═CF—or —C≡C—, and any hydrogen in the alkyl and the alkyl with arbitrary—CH₂— substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—, —CF═CF— or —C≡C—may be substituted with halogen or a C₁₋₃ alkyl; Rings A¹, A², A³, A⁴,and A⁵ are each independently a benzene ring, a naphthalene ring, athiophene ring, a piperidine ring, a cyclohexene ring, a bicyclooctanering, a tetrahydronaphthalene ring or a cyclohexane ring, whereinarbitrary hydrogen in the rings may be substituted with halogen, a C₁₋₃alkyl, a C₁₋₃ alkoxy, or a C₁₋₃ haloalkyl, —CH₂— in the rings may besubstituted with —O— or —S—, and —CH═ in the rings may be substitutedwith —N═; Z⁴, Z⁵, Z⁶, Z⁷, Z⁸, and Z⁹ are each independently a singlebond or a C₁₋₄ alkylene, wherein arbitrary —CH₂— in the alkylene may besubstituted with —O—, —S—, —COO—, —OCO—, —CSO—, —OCS—, —CH═CH—, —CF═CF—or —C≡C—, and arbitrary hydrogen in the alkylene or the alkylene witharbitrary —CH₂— substituted with —O—, —S—, —COO—, —OCO—, —CSO—, —OCS—,—CH═CH—, —CF═CF— or —C≡C— may be substituted with halogen; L⁶, L⁷, andL⁸ are each independently hydrogen or halogen; X² is hydrogen, halogen,—C≡N, —N═C═S, —C≡C—C≡N, —SF₅, or a C₁₋₁₀ alkyl, wherein arbitrary —CH₂—in the alkyl may be substituted with —O—, —S—, —CH═CH— or —C≡C—, andarbitrary hydrogen in the alkyl and the alkyl with arbitrary —CH₂—substituted with —O—, —S—, —CH═CH— or —C≡C— may be substituted withhalogen; and l, m, n, o and p are each independently 0 or 1, providedthat l+m+n+o+p≦4.

[9] The liquid crystal composition according to item 8, in which in thecompound of Formula (2), 2≦l+m+n+o+p≦3.

[10] The liquid crystal composition according to any one of items 1 to6, in which the achiral component T contains only the compound ofFormula (1).

[11] The liquid crystal composition according to any one of items 1 to9, in which the achiral component T contains only 5-95 weight percent(wt %) of the compound of Formula (1) and 5-50 wt % of the compound ofFormula (2).

[12] The liquid crystal composition according to any one of items 1 to9, in which the achiral component T contains 5-95 wt % of the compoundof Formula (1), 5-80 wt % of the compound of Formula (2), and 0-50 wt %of other compounds.

[13] The liquid crystal composition according to any one of items 1 to9, in which the achiral component T contains 5-94 wt % of the compoundof Formula (1), 5-80 wt % of the compound of Formula (2), and 1-50 wt %of other compounds.

[14] The liquid crystal composition according to any one of items 1 to13, in which the achiral component T contains 10-100 wt % of a compoundselected from the group consisting of compounds of Formulas(1-2A)-(1-2H) and Formulas (1-3A)-(1-3D).

(in the formulas, R¹ is a chain selected from Formulas (CHN-1), (CHN-4),(CHN-7), (CHN-8) and (CHN-11); and X¹ is fluorine, chlorine, —CF₃,—CHF₂, —CH₂F, —OCF₃, —OCHF₂, —OCF₂CFHCF₃, or —CH═CHCF₃.)

[15] The liquid crystal composition according to any one of items 1 to14, in which the achiral component T further contains at least onecompound selected from the group consisting of the compounds of Formulas(3), (4), and (5).

(in the formulas, R³ is a C₁₋₁₀ alkyl or a C₂₋₁₀ alkenyl, whereinarbitrary hydrogen in the alkyl and the alkenyl may be substituted withfluorine, and arbitrary —CH₂— in the alkyl, the alkenyl, or the alkyland the alkenyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X³ is fluorine, chlorine, —OCF₃, —OCHF₂, —CF₃,—CHF₂, —CH₂F, —OCF₂CHF₂, or —OCF₂CHFCF₃; Rings B¹, B², and B³ are eachindependently 1,4-cyclohexylene, 1,3-dioxane-2,5-diyl,pyrimidine-2,5-diyl, tetrahydropyran-2,5-diyl, 1,4-phenylene,naphthalene-2,6-diyl, 1,4-phenylene with arbitrary hydrogen substitutedwith fluorine, or naphthalene-2,6-diyl with arbitrary hydrogensubstituted with fluorine or chlorine; in Formula (5), Ring B¹ is1,4-cyclohexylene, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl,tetrahydropyran-2,5-diyl, 1,4-phenylene, naphthalene-2,6-diyl, ornaphthalene-2,6-diyl with arbitrary hydrogen substituted with fluorineor chlorine; Z¹⁰ and Z¹¹ are each independently —(CH₂)₂—, —(CH₂)₄—,—COO—, —CF₂O—, —OCF₂—, —CH═CH—, —C≡C—, —CH₂O—, or a single bond; and L⁹and L¹⁰ are each independently hydrogen or fluorine.)

[16] The liquid crystal composition according to any one of items 1 to14, in which the achiral component T further contains at least onecompound selected from the group consisting of the compound of Formula(6).

(in the formula, R⁴ is a C₁₋₁₀ alkyl or a C₂₋₁₀ alkenyl, whereinarbitrary hydrogen in the alkyl and the alkenyl may be substituted withfluorine, and arbitrary —CH₂— in the alkyl, the alkenyl, or the alkyland the alkenyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X⁴ is —C≡N or —C≡C—C≡N; Rings C¹, C², and C³ areeach independently 1,4-cyclohexylene, 1,4-phenylene, 1,4-phenylene witharbitrary hydrogen substituted with fluorine, naphthalene-2,6-diyl,naphthalene-2,6-diyl with arbitrary hydrogen substituted with fluorineor chlorine, 1,3-dioxane-2,5-diyl, tetrahydropyran-2,5-diyl, orpyrimidine-2,5-diyl; Z¹² is —(CH₂)₂—, —COO—, —CF₂O—, —OCF₂—, —C≡C—,—CH₂O—, or a single bond; L¹¹ and L¹² are each independently hydrogen orfluorine; and r is 0, 1, or 2, s is 0 or 1, and r+s=0, 1 or 2.)

[17] The liquid crystal composition according to any one of items 1 to14, in which the achiral component T further contains at least onecompound selected from the group consisting of compounds of Formulas(7), (8), (9), (10), and (11).

(in the formulas, R⁵ and R⁶ are each independently a C₁₋₁₀ alkyl or aC₂₋₁₀ alkenyl, wherein arbitrary hydrogen in the alkyl and the alkenylmay be substituted with fluorine, and arbitrary —CH₂— in the alkyl, thealkenyl, or the alkyl and the alkenyl with arbitrary hydrogensubstituted with fluorine may be substituted with —O—; Rings D¹, D², D³,and D⁴ are each independently 1,4-cyclohexylene, 1,4-cyclohexenylene,1,4-phenylene, 1,4-phenylene with arbitrary hydrogen substituted withfluorine, tetrahydropyran-2,5-diyl, or decahydronaphthalene-2,6-diyl;Z¹³, Z¹⁴, Z¹⁵, and Z¹⁶ are each independently —(CH₂)₂—, —COO—, —CH₂O—,—OCF₂—, —OCF₂ (CH₂)₂—, or a single bond; L¹³ and L¹⁴ are eachindependently fluorine or chlorine; and t, u, x, y, and z are eachindependently 0 or 1, and u+x+y+z is 1 or 2.)

[18] The liquid crystal composition according to any one of items 1 to14, in which the achiral component T further contains at least onecompound selected from the group consisting of the compounds of Formulas(12), (13), and (14).

(in the formulas, R⁷ and R⁸ are each independently a C₁₋₁₀ alkyl or aC₂₋₁₀ alkenyl, in which arbitrary hydrogen in the alkyl and the alkenylmay be substituted with fluorine, and arbitrary —CH₂— in the alkyl, thealkenyl, or the alkyl and the alkenyl with arbitrary hydrogensubstituted with fluorine may be substituted with —O—; Rings E¹, E², andE³ are each independently 1,4-cyclohexylene, pyrimidine-2,5-diyl,1,4-phenylene, 2-fluoro-1,4-phenylene, 3-fluoro-1,4-phenylene, or2,5-difluoro-1,4-phenylene; Z¹⁷ and Z¹⁸ are each independently —C≡C—,—COO—, —(CH₂)₂—, —CH═CH—, or a single bond.)

[19] The liquid crystal composition according to item 15, furthercontaining at least one compound selected from the group consisting ofthe compound of Formula (6) according to item 16.

[20] The liquid crystal composition according to item 15, furthercontaining at least one compound selected from the group consisting ofthe compounds of Formula (12), (13), and (14) according to item 18.

[21] The liquid crystal composition according to item 16, furthercontaining at least one compound selected from the group consisting ofthe compounds of Formulas (12), (13), and (14) according to item 18.

[22] The liquid crystal composition according to item 17, furthercontaining at least one compound selected from the group consisting ofthe compounds of Formulas (12), (13), and (14) according to item 18.

[23] The liquid crystal composition according to any one of items 1 to14, in which the achiral component T further contains at least onecompound selected from the group consisting of the compounds of Formulas(15), (16), (17), and (18).

(in the formulas, R⁹ is a C₁₋₁₀ alkyl, a C₂₋₁₀ alkenyl, or a C₂₋₁₀alkynyl, in which arbitrary hydrogen in the alkyl, the alkenyl and thealkynyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, the alkynyl, or the alkyl, the alkenyl and thealkynyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X⁵ is fluorine, chlorine, —SF₅, —OCF₃, —OCHF₂,—CF₃, —CHF₂, —CH₂F, —OCF₂CHF₂, or —OCF₂CHFCF₃; Rings F¹, F², F³, and F⁴are each independently 1,4-cyclohexylene, 1,3-dioxane-2,5-diyl,pyrimidine-2,5-diyl, tetrahydropyran-2,5-diyl, 1,4-phenylene,naphthalene-2,6-diyl, 1,4-phenylene with arbitrary hydrogen substitutedwith fluorine or chlorine, or naphthalene-2,6-diyl with arbitraryhydrogen substituted with fluorine or chlorine; in Formulas (17), RingF¹ is 1,4-cyclohexylene, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl,tetrahydropyran-2,5-diyl, 1,4-phenylene, naphthalene-2,6-diyl, ornaphthalene-2,6-diyl with arbitrary hydrogen substituted with fluorineor chlorine; Z¹⁹, Z²⁰, and Z²¹ are each independently —(CH₂)₂—,—(CH₂)₄—, —COO—, —CF₂O—, —OCF₂—, —CH═CH—, —C≡C—, —CH₂O—, or a singlebond; and L¹⁵ and L¹⁶ are each independently hydrogen or fluorine.)

[24] The liquid crystal composition according to any one of items 1 to14, in which the achiral component T further contains at least onecompound selected from the group consisting of the compound of Formula(19).

(in the formulas, R¹⁰ is a C₁₋₁₀ alkyl, a C₂₋₁₀ alkenyl, or a C₂₋₁₀alkynyl, in which arbitrary hydrogen in the alkyl, the alkenyl and thealkynyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, the alkynyl, or the alkyl, the alkenyl and thealkynyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X⁶ is —C≡N, —N═C═S, or —C≡C—C≡N; Rings G¹, G², andG³ are each independently 1,4-cyclohexylene, 1,4-phenylene,1,4-phenylene with arbitrary hydrogen substituted with fluorine orchlorine, naphthalene-2,6-diyl, naphthalene-2,6-diyl with arbitraryhydrogen substituted with fluorine or chlorine, 1,3-dioxane-2,5-diyl,tetrahydropyran-2,5-diyl, or pyrimidine-2,5-diyl; Z²² is —(CH₂)₂—,—COO—, —CF₂O—, —OCF₂—, —C≡C—, —CH₂O—, or a single bond; L¹⁷ and L¹⁸ areeach independently hydrogen or fluorine; and aa is 0, 1 or 2, ab is 0 or1, and aa+ab is 0, 1 or 2.)

[25] The liquid crystal composition according to any one of items 1 to24, containing at least one antioxidant and/or UV absorbent.

[26] The liquid crystal composition according to any one of items 1 to25, in which the optically isotropic liquid crystal phase does notexhibit two or more colors of diffracted light.

[27] The liquid crystal composition according to any one of items 1 to25, in which the optically isotropic liquid crystal phase exhibits twoor more colors of diffracted light.

[28] The liquid crystal composition according to item 26 or 27, obtainedby adding the chiral reagent into a composition having a temperaturedifference of 3° C.-150° C. between an upper-limit temperature and alower-limit temperature of co-existence of a chiral nematic phase and anon-liquid crystal isotropic phase.

[29] The liquid crystal composition according to item 26 or 27, obtainedby adding the chiral reagent into a composition having a temperaturedifference of 5° C.-150° C. between an upper-limit temperature and alower-limit temperature of co-existence of a chiral nematic phase and anon-liquid crystal isotropic phase.

[30] The liquid crystal composition according to item 26 or 27, obtainedby adding the chiral reagent into a composition having a temperaturedifference of 3° C.-150° C. between an upper-limit temperature and alower-limit temperature of co-existence of a nematic phase and anon-liquid crystal isotropic phase.

[31] The liquid crystal composition according to any one of items 1 to30, in which a content of the chiral reagent is 1-40 wt % based on thetotal weight of the liquid crystal composition.

[32] The liquid crystal composition according to any one of items 1 to30, in which a content of the chiral reagent is 5-15 wt % based on thetotal weight of the liquid crystal composition.

[33] The liquid crystal composition according to item 31 or 32,exhibiting a chiral nematic phase at any temperature in the range of 70°C. to −20° C., and having a helical pitch of 700 nm or less within atleast a part of the temperature range.

[34] The liquid crystal composition according to any one of items 31 to33, in which the chiral reagent contains at least one compound selectedfrom the group consisting of the compounds of Formulas (K1)-(K5).

(in Formulas (K1)-(K5), R^(K) is each independently hydrogen, halogen,—C≡N, —N═C═O, —N═C═S, or a C₁₋₂₀ alkyl, wherein arbitrary —CH₂— in thealkyl may be substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—, —CF═CF—or —C≡C—, arbitrary hydrogen in the alkyl may be substituted withhalogen, and additionally, a terminal —CH₃ may be substituted with:

A is each independently an aromatic or non-aromatic 3- to 8-memberedring, or a fused ring having 9 or more carbon atoms, wherein arbitraryhydrogen in the rings may be substituted with halogen, a C₁₋₃ alkyl orhaloalkyl, —CH₂— in the rings may be substituted with —O—, —S—, or —NH—,and —CH═ in the rings may be substituted with —N═; B is eachindependently hydrogen, halogen, a C₁₋₃ alkyl, a C₁₋₃ haloalkyl, anaromatic or non-aromatic 3- to 8-membered ring, or a fused ring having 9or more carbon atoms, wherein arbitrary hydrogen in the rings may besubstituted with halogen, a C₁₋₃ alkyl or haloalkyl, —CH₂— in the ringsmay be substituted with —O—, —S— or —NH—, and —CH═ in the rings may besubstituted with —N═; Z is each independently a single bond, or a C₁₋₈alkylene, wherein arbitrary —CH₂— in the alkylene may be substitutedwith —O—, —S—, —COO—, —OCO—, —CSO—, —OCS—, —N═N—, —CH═N—, —N═CH—,—CH═CH—, —CF═CF—, or —C≡C—, and arbitrary hydrogen in the alkylene maybe substituted with halogen;

X is a single bond, —COO—, —OCO—, —CH₂O—, —OCH₂—, —CF₂O—, —OCF₂—, or—CH₂CH₂—; and

mK is an integer of 1-4.)

[35] The liquid crystal composition according to items 31 to 33, inwhich the chiral reagent contains at least one compound selected fromthe group consisting of the compounds of Formulas (K2-1)-(K2-8),Formulas (K4-1)-(K4-6), and Formulas (K5-1)-(K5-3).

(in the formulas, R^(K) is each independently a C₃₋₁₀ alkyl, wherein—CH₂— adjacent to the ring in the alkyl may be substituted with —O—, andarbitrary —CH₂— in the alkyl may be substituted with —CH═CH—.)

[36] A mixture, containing the liquid crystal composition according toany one of items 1 to 35 and a polymerizable monomer.

[37] The mixture according to item 36, in which the polymerizablemonomer is a photopolymerizable monomer or a thermal-polymerizablemonomer.

[38] A polymer/liquid crystal composite material, obtained bypolymerizing the mixture according to item 36 or 37, for use in a devicedriven in an optically isotropic liquid crystal phase.

[39] The polymer/liquid crystal composite material according to item 38,obtained by polymerizing the mixture according to item 36 or 37 in anon-liquid crystal isotropic phase or an optically isotropic liquidcrystal phase.

[40] The polymer/liquid crystal composite material according to item 38or 39, in which the polymer contained in the polymer/liquid crystalcomposite material has a mesogen moiety.

[41] The polymer/liquid crystal composite material according to any oneof items 38 to 40, in which the polymer contained in the polymer/liquidcrystal composite material has a cross-linked structure.

[42] The polymer/liquid crystal composite material according to any oneof items 38 to 41, in which a content of the liquid crystal compositionis 60-99 wt %, and a content of the polymer is 1-40 wt %.

[44] An optical device, provided with a set of substrates havingelectrodes disposed on either or both surfaces thereof, at least one ofwhich being transparent, a liquid crystal medium disposed between thesubstrates, a polarizer disposed outside of the substrates, and anelectric field-applying means for applying an electric field to theliquid crystal medium via the electrodes, in which the liquid crystalmedium is the liquid crystal composition according to any one of items31 to 35 or the polymer/liquid crystal composite material according toany one of items 38 to 42.

[45] The optical device according to item 43 or 44, in which on at leastone of the set of substrates, the electrodes are configured in a mannersuch that an electric field is applied in at least two directions.

[46] The optical device according to item 43 or 44, in which on one ortwo of the set of substrates disposed in parallel with each other, theelectrodes are configured in a manner such that an electric field isapplied in at least two directions.

[47] The optical device according to any one of items 43 to 46, in whichthe electrodes are configured in a matrix to form pixel electrodes, andeach pixel is provided with an active element being a thin filmtransistor (TFT).

In the present invention, the so-called liquid crystal medium is ageneral term of a liquid crystal composition and a polymer/liquidcrystal composite. Furthermore, as described above, the so-calledoptical device refers to various devices using electro-optic effect toachieve the function of optical modulation or optical switching, forexample, display devices (LCD devices), and optical modulation devicesused in optical communication systems, optical information processing orvarious sensor systems. As for the optical modulation with changes inrefractive index caused by applying a voltage to an optically isotropicliquid crystal medium, the Kerr effect is known. The so-called Kerreffect is a phenomenon, in which the electric birefringence value Δn(E)is proportional to the square of electric field E, that is, Δn(E)=KλE²(K=Kerr coefficient (or Kerr constant), λ: wavelength), for a materialexhibiting the Kerr effect. Herein, the so-called electric birefringencevalue refers to a refractive index anisotropy value induced by applyingan electric field to an isotropic medium.

The terms used in the specification are defined as follows. The liquidcrystal compound is a general term of compounds having a liquid crystalphase such as nematic phase and smectic phase and compounds having noliquid crystal phase but being useful as a component of a liquid crystalcomposition. The chiral reagent is an optically active compound, whichis added to impart the necessary twisted molecular arrangement to aliquid crystal composition. The LCD device is a general term of LCDpanels and LCD modules. The liquid crystal compound, the liquid crystalcomposition, and the LCD device are sometimes simply referred as thecompound, the composition, and the device, respectively. Furthermore,for example, the upper-limit temperature of a liquid crystal phase isthe phase transition temperature from the liquid crystal phase to theisotropic phase, and simply referred as the clearing point orupper-limit temperature. The lower-limit temperature of the liquidcrystal phase is simply referred as the lower-limit temperature. Thecompound of Formula (1) is simply referred as Compound (1), and thesimilar reference is also correspondingly applied to a compound ofFormula (2). In Formulas (1)-(19), the symbols B, D, and E surrounded byhexagons are corresponding to rings B, D, and E, respectively. Thecompound content by percentage is weight percent (wt %) based on thetotal weight of the composition. Numerous identical symbols such asrings A¹, Y¹, or B are included in the same or different formulas;however, the groups represented by these symbols can be identical ordifferent.

“Arbitrary” denotes not only arbitrary position, but also arbitrarynumber, except for the case when the number is 0. The expression thatarbitrary A may be substituted with B, C, or D not only means arbitraryA may be substituted with B, arbitrary A may be substituted with C, andarbitrary A may be substituted with D, but also means that a pluralityof A may be substituted with at least two of B-D. For example, the alkylin which arbitrary —CH₂— may be substituted with —O— or —CH═CH— includesalkyl, alkenyl, alkoxy, alkoxyalkyl, alkoxyalkenyl, alkenyloxyalkyl, andso on. Furthermore, in the present invention, two contiguous —CH₂— beingsubstituted with —O— to form —O—O— is unsuitable, and the terminal —CH₂—in an alkyl being substituted with —O— is also unsuitable. The presentinvention will be further described below. The terminal groups, rings,and linking groups of the compound of Formula (1) will also beillustrated with preferred examples.

[Effects of the Invention]

The liquid crystal composition of the present invention is stable toheat and light, and has an optically isotropic liquid crystal phasehaving a high upper-limit temperature and a low lower-limit temperature,and has a low driving voltage when being used in a device driven in anoptically isotropic liquid crystal phase. The polymer/liquid crystalcomposite material of the present invention includes a material of anoptically isotropic liquid crystal phase that exhibits a highupper-limit temperature and a low lower-limit temperature, and has a lowdriving voltage when being used in a device driven in an opticallyisotropic liquid crystal phase.

The optical device of the present invention driven in an opticallyisotropic liquid crystal phase has a wide usable temperature range, ashort response time, a high contrast, and a low driving voltage.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a comb-like electrode substrate used in an embodiment.

FIG. 2 shows an optical system used in an embodiment.

DESCRIPTION OF THE EMBODIMENTS

1-1 Compound (1)

The liquid crystal composition exhibiting an optically isotropic liquidcrystal phase of the present invention contains an achiral component Tand a chiral reagent, wherein the achiral component T contains acompound of Formula (1) as Component A. A first aspect of the presentinvention is that the achiral component T contains only Component A, theachiral component T contains Component A and Component B of Formula (2),the achiral component T contains Component A and other components notspecifically disclosed in the specification, or the achiral component Tcontains Component A, Component B, and other components not specificallydisclosed in the specification. In order for the liquid crystalcomposition of the present invention to exhibit excellent properties, itis preferred that 0.1-100 wt % of at least one of the compound ofFormula (1) of the present invention is contained as the achiralcomponent T.

The compound of Formula (1) is described.

In Formulas (1), R¹ is hydrogen or a C₁₋₂₀ alkyl, wherein arbitrary—CH₂— in the alkyl may be substituted with —O—, —S—, —COO—, —OCO—,—CH═CH—, —CF═CF— or —C≡C—, and arbitrary hydrogen in the alkyl and thealkyl with arbitrary —CH₂— substituted with —O—, —S—, —COO—, —OCO—,—CH═CH—, —CF═CF— or —C≡C— may be substituted with halogen or a C₁₋₃alkyl; Z¹, Z², and Z³ are each independently a single bond, —COO—, or—CF₂O—, provide that at least one of Z¹, Z², and Z³ is —CF₂O—; L¹, L²,L³, L⁴, and L⁵ are each independently hydrogen or fluorine; X¹ ishydrogen, halogen, —SF₅, or a C₁₋₁₀ alkyl, wherein arbitrary —CH₂— inthe alkyl may be substituted with —O—, —S—, —CH═CH—, or —C≡C—, andarbitrary hydrogen in the alkyl or the alkyl with arbitrary —CH₂—substituted with —O—, —S—, —CH═CH— or —C≡C— may be substituted withfluorine.

As for such a R¹, a linear group is preferred to a branched group. Apreferred stereo configuration of —CH═CH— in alkenyl depends on theposition of the double bond. A trans-configuration is preferred for suchan alkenyl having a double bond at an odd position, such as —CH═CHCH₃,—CH═CHC₂H₅, —CH═CHC₃H₇, —CH═CHC₄H₉, —C₂H₄CH═CHCH₃, and —C₂H₄CH═CHC₂H₅. Acis-configuration is preferred for such an alkenyl having a double bondat an even position, such as —CH₂CH═CHCH₃, —CH₂CH═CHC₂H₅, and—CH₂CH═CHC₃H₇. An alkenyl compound having a preferred stereoconfiguration has a high upper-limit temperature or has a liquid crystalphase over a wide temperature range, as illustrated in detail in Mol.Cryst. Liq. Cryst., 1985, 131, 109 and Mol. Cryst. Liq. Cryst., 1985,131, 327.

The alkyl may be linear or branched, and specific examples include —CH₃,—C₂H₅, —C₃H₇, —C₄H₉, —C₅H₁₁, —C₆H₁₃, —C₇H₁₅, —C₈H₁₇, —C₉H₁₉, —C₁₀H₂₁,—C₁₁H₂₃, —C₁₂H₂₅, —C₁₃H₂₇, —C₁₄H₂₉, and —C₁₅H₃₁.

The alkoxy may be linear or branched, and specific examples include—OCH₃, —OC₂H₅, —OC₃H₇, —OC₄H₉, —OC₅H₁₁, —OC₆H₁₃, —OC₇H₁₅, —OC₈H₁₇,—OC₉H₁₉, —OC₁₀H₂₁, —OC₁₁H₂₃, —OC₁₂H₂₅, —OC₁₃H₂₇, and —OC₁₄H₂₉.

The alkoxyalkyl may be linear or branched, and specific examples include—CH₂OCH₃, —CH₂OC₂H₅, —CH₂OC₃H₇, —(CH₂)₂—OCH₃, —(CH₂)₂—OC₂H₅,—(CH₂)₂—OC₃H₇, —(CH₂)₃—OCH₃, —(CH₂)₄—OCH₃, and —(CH₂)₅—OCH₃.

The alkenyl may be linear or branched, and specific examples include—CH═CH₂, —CH═CHCH₃, —CH₂CH═CH₂, —CH═CHC₂H₅, —CH₂CH═CHCH₃,—(CH₂)₂—CH═CH₂, —CH═CHC₃H₇, —CH₂CH═CHC₂H₅, —(CH₂)₂—CH═CHCH₃, and—(CH₂)₃—CH═CH₂.

The alkenyloxy may be linear or branched, and specific examples include—OCH₂CH═CH₂, —OCH₂CH═CHCH₃, and —OCH₂CH═CHC₂H₅.

The alkynyl may be linear or branched, and specific examples include—C≡CH, —C≡CCH₃, —CH₂C≡CH, —C≡CC₂H₅, —CH₂C≡CCH₃, —(CH₂)₂—C≡CH, —C≡CC₃H₇,—CH₂C≡CC₂H₅, —(CH₂)₂—C≡CCH₃, and —C≡C(CH₂)₅.

Preferably, R¹ has a structure of Formulas (CHN-1)-(CHN-19). Herein,R^(1a) is hydrogen, or a C₁₋₂₀ alkyl. More preferably, R¹ has astructure of Formulas (CHN-1)-(CHN-4) or Formulas (CHN-6)-(CHN-7).

In Formula (1), Z¹, Z², and Z³ are each independently a single bond,—COO—, or —CF₂O—, provided that at least one of Z¹, Z², and Z³ is—CF₂O—.

Preferred examples of Z¹, Z², and Z³ include a single bond and —CF₂O—.

In Formula (1), L¹, L², L³, L⁴, and L⁵ are each independently hydrogenor fluorine. Furthermore, preferably L² and L⁴ are fluorine, and morepreferably, L², L⁴ and L⁵ are fluorine.

In Formula (1), X¹ is hydrogen, halogen, —SF₅, or a C₁₋₁₀ alkyl, whereinarbitrary —CH₂— in the alkyl may be substituted with —O—, —S—, —CH═CH—or —C≡C—, and arbitrary hydrogen in the alkyl and the alkyl witharbitrary —CH₂— substituted with —O—, —S—, —CH═CH— or —C≡C— may besubstituted with fluorine.

Specific examples of the alkyl with arbitrary hydrogen substituted withhalogen include —CH₂F, —CHF₂, —CF₃, —(CH₂)₂—F, —CF₂CH₂F, —CF₂CHF₂,—CH₂CF₃, —CF₂CF₃, —(CH₂)₃—F, —(CF₂)₃—F, —CF₂CHFCF₃, —CHFCF₂CF₃,—(CH₂)₄—F, —(CF₂)₄—F, —(CH₂)₅—F, and —(CF₂)₅—F.

Specific examples of alkoxy with arbitrary hydrogen substituted withhalogen include —OCH₂F, —OCHF₂, —OCF₃, —O—(CH₂)₂—F, —OCF₂CH₂F,—OCF₂CHF₂, —OCH₂CF₃, —O—(CH₂)₃—F, —O—(CF₂)₃—F, —OCF₂CHFCF₃, —OCHFCF₂CF₃,—O(CH₂)₄—F, —O—(CF₂)₄—F, —O—(CH₂)₅—F, and —O—(CF₂)₅—F.

Specific examples of alkenyl with arbitrary hydrogen substituted withhalogen include —CH═CHF, —CH═CF₂, —CF═CHF, —CH═CHCH₂F, —CH═CHCF₃,—(CH₂)₂—CH═CF₂, —CH₂CH═CHCF₃, —CH═CHCF₃, and —CH═CHCF₂CF₃.

Specific examples of X¹ include hydrogen, fluorine, chlorine, —C≡N,—N═C═S, —SF₅, —CH₃, —C₂H₅, —C₃H₇, —C₄H₉, —C₅H₁₁, —C₆H₁₃, —C₇H₁₅, —C₈H₁₇,—C₉H₁₉, —C₁₀H₂₁, —CH₂F, —CHF₂, —CF₃, —(CH₂)₂—F, —CF₂CH₂F, —CF₂CHF₂,—CH₂CF₃, —CF₂CF₃, —(CH₂)₃—F, —(CF₂)₃—F, —CF₂CHFCF₃, —CHFCF₂CF₃,—(CH₂)₄—F, —(CF₂)₄—F, —(CH₂)₅—F, —(CF₂)₅—F, —OCH₃, —OC₂H₅, —OC₃H₇,—OC₄H₉, —OC₅H₁₁, —OCH₂F, —OCHF₂, —OCF₃, —O—(CH₂)₂—F, —OCF₂CH₂F,—OCF₂CHF₂, —OCH₂CF₃, —O—(CH₂)₃—F, —O—(CF₂)₃—F, —OCF₂CHFCF₃, —OCHFCF₂CF₃,—O(CH₂)₄—F, —O—(CF₂)₄—F, —O—(CH₂)₅—F, —O—(CF₂)₅—F, —CH═CH₂, —CH═CHCH₃,—CH₂CH═CH₂, —CH═CHC₂H₅, —CH₂CH═CHCH₃, —(CH₂)₂—CH═CH₂, —CH═CHC₃H₇,—CH₂CH═CHC₂H₅, —(CH₂)₂—CH═CHCH₃, —(CH₂)₃—CH═CH₂, —CH═CHF, —CH═CF₂,—CF═CHF, —CH═CHCH₂F, —CH═CHCF₃, —(CH₂)₂—CH═CF₂, —CH═CHCF₃, —CH₂CH═CHCF₃,and —CH═CHCF₂CF₃.

Preferred examples of X¹ include fluorine, chlorine, —CF₃, —CHF₂, —OCF₃,and —OCHF₂. Most preferred examples of X¹ include fluorine, chlorine,—CF₃, and —OCF₃.

In Formula (1), structures of Formulas (1-1)-(1-3) are preferred.

In the formulas, R¹ has a structure of any one of Formulas(CHN-1)-(CHN-19), R^(1a) is hydrogen, or a C₁₋₂₀ alkyl; L¹, L², L³, L⁴,and L⁵ are each independently hydrogen or fluorine; and X¹ is fluorine,chlorine, —CF₃, —CHF₂, —OCF₃, —OCHF₂, —C≡C—CF₃, —CH═CHCF₃, or—OCF₂CFHCF₃.

1-2 Properties of Compound (1)

Compound (1) used in the present invention is further described indetail. Compound (1) is a compound having four benzene rings and atleast one linking group —CF₂O—, which has very stable physical andchemical properties under the conditions where the device isconventionally used, and has an excellent compatibility with otherliquid crystal compounds. The composition containing such a compound isstable under the conditions where the device is conventionally used.Therefore, the composition containing the compound has an expandedtemperature range of an optically isotropic liquid crystal phase, andthus can be used in a display device over a wide temperature range.Moreover, due to large dielectric anisotropy and large refractive indexanisotropy, the compound may be used as a component for lowering thedriving voltage of a composition driven in an optically isotropic liquidcrystal phase.

By properly selecting the left terminal group R¹, the groups on thebenzene rings (L¹-L⁵, and X¹), or the linking groups Z¹-Z³ in Compound(1), the physical properties such as clearing point, refractive indexanisotropy, and dielectric anisotropy can be adjusted at will. Theeffects of the types of the left terminal group R¹, the groups on thebenzene rings (L¹-L⁵, and X¹), or the linking groups Z¹-Z³ on thephysical properties of Compound (1) will be described below.

When R¹ is linear, Compound (1) has a liquid crystal phase over a widetemperature range and a low viscosity. When R¹ is branched, Compound (1)has good compatibility with other liquid crystal compounds. When R¹ isan alkenyl, a preferred stereo configuration depends on the position ofthe double bond. An alkenyl compound having a preferred stereoconfiguration has a high upper-limit temperature or has a liquid crystalphase with over a wide temperature range.

When the linking groups Z¹, Z², and Z³ are a single bond or —CF₂O—,Compound (1) has a low viscosity. When the linking groups Z¹, Z², and Z³are —COO—, or —CF₂O—, Compound (1) has a large dielectric anisotropy.When the linking groups Z¹, Z², and Z³ are a single bond, or —CF₂O—,Compound (1) has stable chemical properties, and is unlikely to bedeteriorated.

When the right terminal group X¹ is fluorine, chlorine, —SF₅, —CF₃,—CHF₂, —CH₂F, —OCF₃, —OCHF₂, or —OCH₂F, Compound (1) has a largedielectric anisotropy. When X¹ is fluorine, —OCF₃, or —CF₃, Compound (1)has stable chemical properties.

When the number of L¹-L⁵, which is fluorine, is large, Compound (1) hasa large dielectric anisotropy. When L¹ is hydrogen, Compound (1) hasexcellent compatibility with other liquid crystal compounds. When L⁴ andL⁵ are both fluorine, Compound (1) has an especially large dielectricanisotropy.

As described above, a compound with target properties can be obtained byproperly selecting the types of the terminal groups, linking groups, andthe like.

1-3 Specific Examples of Compound (1)

Preferred examples of Compound (1) include Formulas (1-1)-(1-3). Morepreferred examples include Formulas (1-2A)-(1-2H), and Formulas(1-3A)-(1-3C). Further more preferred examples include Formulas(1-2A)-(1-2D), (1-3A), and (1-3B). Most preferred examples includeFormulas (1-2A) and (1-2C).

(in the formulas, R¹ is a chain selected from Formulas (CHN-1), (CHN-4),(CHN-7), (CHN-8), and (CHN-11); X¹ is fluorine, chlorine, —CF₃, —CHF₂,—CH₂F, —OCF₃, —OCHF₂, —OCF₂CFHCF₃, or —CH═CHCF₃.)

1-4Synthesis of Compound (1)

Next, the synthesis of Compound (1) is described. Compound (1) may besynthesized by a suitable combination of organic synthesis methods. Themethods for introducing target terminal groups, rings, and linkinggroups into a starting compound are described in, for example, OrganicSyntheses John Wiley & Sons, Inc, Organic Reactions, John Wiley & Sons,Inc, Comprehensive Organic Synthesis, Pergamon Press, and New Lectureson Experimental Chemistry (Maruzen).

1-4-2 Methods for Generating Linking Groups Z¹-Z³

An example of the methods for generating the linking groups Z¹-Z³ inCompound (1) is as shown in a scheme below. In the scheme, MSG¹ or MSG²is monovalent organic group having at least one ring. The multiple MSGs¹(or MSGs²) in the scheme may be identical or different. Compounds(1A)-(1J) are equivalent to Compound (1).

Subsequently, as for the linking groups Z¹-Z³ in Compound (1),generation methods of various bonds are described in Sections (I)-(III)below.

(I) Generation of a Single Bond

Arylboronic acid (20) is reacted with Compound (21) synthesized via awell-known process in an aqueous carbonate solution in presence of acatalyst such as tetrakis(triphenylphosphine)palladium, to synthesizeCompound (1A). Compound (1A) may also be synthesized by reactingCompound (22) synthesized via a well-known process with n-butyl lithium,then with zinc chloride, and finally with Compound (21) in the presenceof a catalyst such as bis(triphenylphosphine)palladium dichloride.

(II) Generation of —COO— and —OCO—

Compound (22) is reacted with n-butyl lithium, and then with carbondioxide, to obtain a carboxylic acid (23). Compound (23) and phenol (24)synthesized via a well-known process are dehydrated in the presence of1,3-dicyclohexylcarbodiimide (DCC) and 4-dimethylaminopyridine (DMAP),to synthesize Compound (1B) having —COO—. A compound having —OCO— mayalso be synthesized through this method.

(III) Generation of —CF₂O— and —OCF₂—

Compound (1B) is treated with a thionating agent such as Lawesson'sReagent, to obtain Compound (25). Compound (25) is florinated by usinghydrogen fluoride pyridine complex and N-bromosuccinimide (NBS), tosynthesize Compound (1C) having —CF₂O—. See M. Kuroboshi et al., Chem.Lett., 1992, 827. Compound (1C) may also be synthesized by fluorinatingCompound (25) with (diethylamino)sulfurtrifluoride (DAST). See W. H.Bunnelle et al., J. Org. Chem. 1990, 55, 768. A compound having —OCF₂—may also be synthesized through this method. The linking groups may alsobe generated by the method described in Peer. Kirsch et al., Angew.Chem. Int. Ed. 2001, 40, 1480.

1-4-4 Methods for Synthesizing Compound (1)

There are many methods for synthesizing the compounds of Formula (1),and they may be synthesized from commercially available reagents, withproper reference to examples in the specification, or documents andbooks.

1-4-5 Methods for Synthesizing Compound (2)

There are many methods for synthesizing the compounds of Formula (2),and they may be synthesized from commercially available reagents, withproper reference to examples in the specification, or documents andbooks.

2 Compounds (2)-(18)

A second aspect of the present invention is a liquid crystal compositioncontaining an achiral component T and a chiral reagent, wherein theachiral component T is obtained by adding a component selected fromComponents B, C, D, and E below into Component A formed of the compoundof Formula (1). Compared with a composition with an achiral component Tcontaining Component A alone, the liquid crystal composition may befreely adjusted for the driving voltage, the temperature range of aliquid crystal phase, the refractive index anisotropy value, thedielectric anisotropy value, and viscosity.

The component added into the Component A is preferably obtained bymixing Components B, C, D, or E, where Component B contains at least onecompound selected from the group consisting of the compounds of Formula(2), Component C contains at least one compound selected from the groupconsisting of the compounds of Formulas (3), (4), and (5), Component Dcontains at least one compound selected from the group consisting of thecompounds of Formula (6), and Component E contains at least one compoundselected from the group consisting of the compounds of Formulas (7),(8), (9), (10), and (11).

Moreover, by mixing Component F containing at least one compoundselected from the group consisting of the compounds of Formulas (12),(13), and (14), the threshold voltage, the temperature range of a liquidcrystal phase, the refractive index anisotropy value, the dielectricanisotropy value, and the viscosity may be adjusted.

The component added into the Component A is preferably Component Gcontaining at least one compound selected from the group consisting ofthe compounds of Formulas (15), (16), and (17), or Component Hcontaining at least one compound selected from the group consisting ofthe compounds of Formula (18). Components G and H are especially usefulfor improving the refractive index anisotropy value and the dielectricanisotropy value.

Moreover, for each component of the liquid crystal composition used inthe present invention, an analogue containing isotopes of each elementmay be used, because no significant difference in physical propertiesexists.

In Component B above, preferred examples of the compound of Formula (2)include Formulas (2-1)-(2-9).

(in the formulas, R² and X² have the same meaning as R² and X² inFormula (2).)

In Component C, preferred examples of the compound of Formula (3)include Formulas (3-1)-(3-16), preferred examples of the compound ofFormula (4) include Formulas (4-1)-(4-112), and preferred examples ofthe compound of Formula (5) include Formulas (5-1)-(5-52).

(in the formulas, R³, and X³ having the same meanings as those of R³,and X³ in Formulas (3)-(5).)

The compounds of Formulas (3)-(5) (i.e. Component C) have a positivedielectric anisotropy value and excellent thermal or chemical stability,and thus are useful for preparing a liquid crystal composition for TFTs.Based on the total weight of the liquid crystal composition of thepresent invention, the content of Component C in the liquid crystalcomposition of the present invention is suitably in a range of 1-99 wt%, preferably 1-60 wt %, and more preferably 1-35 wt %. Furthermore, byfurther containing the compounds of Formulas (12)-(14) (i.e., ComponentF), the viscosity may be adjusted.

Preferred examples of the compound of Formula (6) (i.e. Component D)include Formulas (6-1)-(6-62).

(in the formulas, R⁴ and X⁴ have the same meanings as those of R⁴ and X⁴in Formula (6).)

The compounds of Formula (6) (i.e., Component D) have a positive andvery large dielectric anisotropy value. By containing Component D, thedriving voltage of the composition is lowered. In addition, theviscosity and refractive index anisotropy value can be adjusted, and thetemperature range of a liquid crystal phase can be expanded.

Based on the total weight of the composition, the content of Component Dis preferably 0.1-99.9 wt %, more preferably 1-97 wt %, and still morepreferably 1-30 wt %. Furthermore, by mixing the components below, thethreshold voltage, the temperature range of a liquid crystal phase, therefractive index anisotropy value, dielectric anisotropy value, and theviscosity may be adjusted.

Component E containing at least one compound selected from the groupconsisting of the compounds of Formulas (7)-(11) is a preferredcomponent for preparing the liquid crystal composition of the presentinvention having a negative dielectric anisotropy value.

Preferred examples of the compounds of Formulas (7)-(11) (Component E)are respectively Formulas (7-1)-(7-5), Formulas (8-1)-(8-9), Formulas(9-1)-(9-3), and Formulas (11-1)-(11-11).

(in the formulas, R⁵ and R⁶ have the meanings as those of R⁵ and R⁶ inFormulas (7)-(11).)

The compounds of the Component E are mainly used in the liquid crystal

compositions having a negative dielectric anisotropy value. In ComponentE, the compound of Formula (7) is a bicyclic compound, thereby mainlyhaving the effect of adjusting the threshold voltage, the viscosity, orthe refractive index anisotropy value. Furthermore, the compounds ofFormulas (8) and (9) are tricyclic compounds, thereby having the effectof increasing the clearing point, expanding the temperature range of anoptically isotropic liquid crystal phase, and increasing the refractiveindex anisotropy value. The compounds of Formulas (10) and (11) have anegative and large dielectric anisotropy value, thereby mainly havingthe effect of adjusting the driving voltage.

In preparing a composition having a negative dielectric anisotropyvalue, the content of Component E is preferably higher than or equal to40 wt %, and more preferably in the range of 50 wt %-95 wt %, based onthe total weight of the composition. Furthermore, by mixing Component E,the elastic constant and the voltage-transmittance curve of thecomposition may be controlled. When mixing Component E into acomposition having a positive dielectric anisotropy value, the contentof Component E is preferably lower than or equal to 30 wt %, based onthe total weight of the composition.

Preferred examples of the compounds of Formulas (12), (13), and (14)(Component F) include respectively Formulas (12-1)-(12-11), Formulas(13-1)-(13-18), and Formulas (14-1)-(14-6).

(in the formulas, R⁷ and R⁸ have the same meaning as R⁷ and R⁸ inFormulas (12)-(14).)

The compounds of Formulas (12)-(14) (Component F) are compounds having alow absolute value of dielectric anisotropy, and are nearly neutral. Thecompounds of Formula (12) mainly have the effect of adjusting theviscosity or the refractive index anisotropy value. Furthermore, thecompounds of Formulas (13) and (14) have the effect of increasing theclearing point and expanding the temperature range of an opticallyisotropic liquid crystal phase, or the effect of adjusting therefractive index anisotropy value.

If the content of the compounds of Component F is increased, the drivingvoltage of the liquid crystal composition is raised, and the viscosityis lowered. Therefore, the content of the compounds of Component E isexpected to be as high as possible, provided that the desired drivingvoltage of the liquid crystal composition is met. In preparing a liquidcrystal composition for a TFT, the content of Component F is preferably60 wt % or less, and more preferably 40 wt % or less, based on the totalweight of the composition.

3 Compound (15)-Compound (19)

A third aspect of the present invention is a liquid crystal compositionobtained by adding a component selected from Components G and H belowinto Component A.

The component added into Component A is preferably obtained by mixingComponent G or H, where Component G contains at least one compoundselected from the group consisting of the compounds of Formulas (15),(16), (17), and (18), and Component H contains at least one compoundselected from the group consisting of the compounds of Formulas (19).

Moreover, for each component of the liquid crystal composition of thepresent invention, an analogue containing isotopes of each element alsocan be used, because no significant difference in physical propertiesexists.

In Component G, preferred examples of the compounds of Formula (15)include Formulas (15-1)-(15-8), preferred examples of the compounds ofFormula (16) include Formulas (16-1)-(16-26), preferred examples of thecompounds of Formula (17) include Formulas (17-1)-(17-13), and preferredexamples of the compounds of Formula (18) include Formulas(18-1)-(18-12). Formulas (17-7), and (17-8) have the effect of expandingthe temperature range at a low temperature side.

(in the formulas, R⁹ and X⁵ have the same meaning as R⁹ and X⁵ inFormulas (15)-(18), (F) denotes hydrogen or fluorine, and (F, Cl)denotes hydrogen, fluorine or chlorine.)

The compounds of Formulas (15)-(18) (i.e. Component G) have a positiveand very large dielectric anisotropy value and excellent thermal orchemical stability, thereby being suitable for preparing a liquidcrystal composition used in active driving, such as TFT driving. In theliquid crystal composition of the present invention, the content ofComponent G is suitably in the range of 1 wt %-99 wt %, preferably 10 wt%-97 wt %, and more preferably 20 wt %-95 wt %, based on the totalweight of the liquid crystal composition of the present invention.Furthermore, by further containing the compounds of Formulas (12)-(14)(Component F), the viscosity may be adjusted.

Preferred examples of the compounds of Formula (19) (i.e. Component H)include Formulas (19-1)-(19-37).

(in the formulas, R¹⁰ and X⁶ have the same meaning as R¹⁰ and X⁶ inFormula (19), (F) denotes hydrogen or fluorine, and (F, Cl) denoteshydrogen, fluorine, or chlorine.)

The compounds of Formula (19) (i.e., Component H) have a positive andvery large dielectric anisotropy value, thereby mainly being used tolower the driving voltage of the devices. By containing Component H, thedriving voltage of the composition is lowered, as well as the viscosityand the refractive index anisotropy value may be adjusted, and thetemperature range of a liquid crystal phase is expanded. Moreover, thesteepness is also improved.

The content of Component H is preferably in the range of 0.1 wt %-99.9wt %, more preferably 1 wt %-97 wt %, and more preferably 1 wt %-45 wt%, based on the total weight of the composition.

The liquid crystal composition of the present invention may be preparedgenerally through a well-known method, for example, by dissolving therequired components at a high temperature.

4 Composition Having Optically Isotropic Liquid Crystal Phase

4.1 Composition of Composition Having Optically Isotropic Liquid CrystalPhase

A fourth aspect of the present invention is a composition containing thecompound of Formula (1) and a chiral reagent, which is a liquid crystalcomposition useful in an optical device driven in an optically isotropicliquid crystal phase and exhibiting an optically isotropic liquidcrystal phase.

Although being a tetracyclic compound, the compound of Formula (1) has alow clearing point, and a large dielectric anisotropy and a largerefractive index anisotropy; therefore, in order to exhibit excellentproperties, the content of the compound of Formula (1) is preferably0.1-100 wt % based on the total weight of the achiral component Twithout the chiral reagent. The content of the compound of Formula (1)is more preferably 5-100 wt %, still preferably 30-100 wt %, and stillmore preferably 70-100 wt %.

Furthermore, the compound of Formula (1-2) have good compatibility withother liquid crystal compositions, and thus the content thereof may be5-100 wt %, preferably 20-100 wt %, and more preferably 20-80 wt %,based on the total weight of the achiral component T.

Based on the total weight of the liquid crystal composition of thepresent invention, the content of the chiral reagent is preferably 1-40wt %, more preferably 3-25 wt %, and most preferably 5-15 wt %. A liquidcrystal composition containing the chiral reagent in these ranges tendsto have an optically isotropic liquid crystal phase, and thus ispreferred.

The chiral reagent contained in the liquid crystal composition may beone, two, or more.

4.2 Chiral Reagent

The chiral reagent contained in the optically isotropic liquid crystalcomposition is not particularly limited, provided that it is anoptically active compound capable of twisting the liquid crystalcomposition after being added into the achiral component T. The chiralreagent is preferably a compound with a large helical twisting power. Asa compound with a large helical twisting power reduces the adding amountrequired for obtaining a desired pitch, a rise in the driving voltagecan be suppressed, which is advantageous in practice. Specifically, thecompounds of Formulas (K1)-(K5) below are preferred.

(in Formulas (K1)-(K5), R^(K) is each independently hydrogen, halogen,—C≡N, —N═C═O, —N═C═S, or a C₁₋₂₀ alkyl, in which arbitrary —CH₂— may besubstituted with —O—, —S—, —COO—, —OCO—, —CH═CH—, —CF═CF— or —C≡C—,arbitrary hydrogen may be substituted with halogen, and terminal —CH₃may be substituted with

A is each independently an aromatic or non-aromatic 3- to 8-memberedring, or a fused ring having 9 or more carbon atoms, wherein arbitraryhydrogen in the rings may be substituted with halogen or a C₁₋₃ alkyl orhaloalkyl, —CH₂— in the rings may be substituted with —O—, —S— or —NH—,and —CH═ in the rings may be substituted with —N═; B is eachindependently hydrogen, halogen, a C₁₋₃ alkyl, a C₁₋₃ haloalkyl, anaromatic or non-aromatic 3- to 8-membered ring, or a fused ring having 9or more carbon atoms, wherein arbitrary hydrogen in the rings may besubstituted with halogen or a C₁₋₃ alkyl or haloalkyl, —CH₂— in therings may be substituted with —O—, —S— or —NH—, and —CH═ in the ringsmay be substituted with —N═; and Z is each independently a single bond,or a C₁₋₈ alkylene, wherein arbitrary —CH₂— in the alkylene may besubstituted with —O—, —S—, —COO—, —OCO—, —CSO—, —OCS—, —N═N—, —CH═N—,—N═CH—, —CH═CH—, —CF═CF— or —C≡C—, and arbitrary hydrogen in thealkylene may be substituted with halogen;

X is a single bond, —COO—, —OCO—, —CH₂O—, —OCH₂—, —CF₂O—, —OCF₂— or—CH₂CH₂—;

mK is an integer of 1-4. Moreover, when two or more R^(K), A, Z, and mKexist, the R^(K), A, Z, and mK may be identical or different.)

Among the compounds, the chiral reagent added into the liquid crystalcomposition is preferably Formulas (K2-1)-(K2-8) included in Formula(K2), Formulas (K4-1)-(K4-6) included in Formula (K4), and Formulas(K5-1)-(K5-3) included in Formula (K5).

(in the formulas, R^(K) is each independently a C₃₋₁₀ alkyl, in which—CH₂—adjacent to the ring in the alkyl may be substituted with —O—, andarbitrary —CH₂— in the alkyl or the alkyl with —CH₂— adjacent to thering substituted with —O— may be substituted with —CH═CH—.)

4.3 Optically Isotropic Liquid Crystal Phase

The so-called liquid crystal composition having optically isotropy meansthat the composition exhibits an optical isotropy because the liquidcrystal molecules macroscopically have an isotropic arrangement, butmicroscopically a liquid crystal order exists. “Pitch corresponding tothe microscopic liquid crystal order of the liquid crystal composition(sometimes referred to as pitch, hereafter)” is preferably 700 nm orless, more preferably 500 nm or less, and most preferably 350 nm orless.

Herein, the so-called “non-liquid crystal isotropic phase” refers to acommonly defined isotropic phase (i.e. disordered phase), and refers toan isotropic phase where a region with a non-zero local order parameteris generated due to fluctuation. For example, an isotropic phaseexhibited at a high temperature side of a nematic phase is equivalent tothe non-liquid crystal isotropic phase in the specification. The chiralliquid crystal in the specification also has a similar definition.Moreover, the so-called “optically isotropic liquid crystal phase” inthe specification means a phase that exhibits an optical isotropywithout fluctuation, an example of which is a phase exhibiting aplatelet tissue (i.e. blue phase in narrow sense).

The optically isotropic liquid crystal composition of the presentinvention has an optically isotropic liquid crystal phase. However, thetypical platelet tissue is not observed in the blue phase under apolarizing microscope sometimes. Therefore, in the specification, aphase exhibiting the platelet tissue is designated as blue phase, and anoptically isotropic liquid crystal phase including the blue phase isdesignated as optically isotropic liquid crystal phase. That is, theblue phase is included in the optically isotropic liquid crystal phase.

Generally, the blue phase is divided into three types, that is, bluephase I, blue phase II, and blue phase III, and all the three bluephases are optically active and isotropic. In the blue phase I or bluephase II, two or more diffracted lights produced by the Bragg reflectionfrom different lattice planes are observed. The blue phase is generallyobserved between the non-liquid crystal isotropic phase and the chiralnematic phase.

The so-called state that the optically isotropic liquid crystal phasedoes not exhibit two or more colors of diffracted light means that aplatelet tissue observed in the blue phase I and blue phase II is notobserved and the phase exhibits substantially a single color in theentire plane. For an optically isotropic liquid crystal phase notexhibiting two or more colors of diffracted light, brightness/darknessof the colors is not necessarily to be even in plane.

The optically isotropic liquid crystal phase not exhibiting two or morecolors of diffracted light has the advantage of inhibiting the intensityof reflected light caused by Bragg reflection, or shifting the reflectedlight toward the low wavelength side.

Furthermore, when a liquid crystal material reflecting visible light isused in a display device, a color variation problem may sometimes occur.However, for a liquid crystal not exhibiting two or more colors ofdiffracted light, because reflection wavelength shift toward the lowwavelength side, the reflection of visible light may be eliminated bythe pitch longer than that in the blue phase in a narrow sense (a phaseexhibiting the platelet tissue).

The optically isotropic liquid crystal composition of the presentinvention may be obtained by adding a chiral reagent into a compositionhaving a nematic phase. In this case, the chiral reagent is preferablyadded in a concentration such that the pitch is 700 nm or less.Furthermore, the composition having a nematic phase contains thecompound of Formula (1) and other optional components. Moreover, theoptically isotropic liquid crystal composition of the present inventioncan also be obtained by adding a chiral reagent to a composition havinga chiral nematic phase but no optically isotropic liquid crystal phase.Furthermore, the composition having a chiral nematic phase but nooptically isotropic liquid phase contains the compound of Formula (1),an optically active compound, and other optional components. In thiscase, the optically active compound is preferably added in aconcentration such that the pitch is 700 nm or more, so as not toexhibit an optically isotropic liquid crystal phase. Here, the opticallyactive compounds to be added may be the compounds with a large helicaltwisting power above, that is, the compounds of Formulas (K-1)-(K-5),Formulas (K2-1)-(K2-8), or Formulas (K5-1)-(K5-3). Moreover, theoptically active compound added may not have a large helical twistingpower. Such an optically active compound is, for example, one added in aliquid crystal composition for a device driven in a nematic phase (TNmode, STN mode, and the like).

Examples of the optically active compound without a large helicaltwisting power are the following optically active compounds(Op-1)-(Op-13).

Moreover, the temperature range of the optically isotropic liquidcrystal composition of the present invention may be expanded by adding achiral reagent into a liquid crystal composition having the co-existenceof a nematic phase or a chiral nematic phase over a wide temperaturerange and an isotropic phase for exhibiting an optically isotropicliquid crystal phase. For example, a composition exhibiting an opticallyisotropic liquid crystal phase in a wide temperature range can beprepared as follows: a liquid crystal compound having a high clearingpoint is mixed with a liquid crystal compound having a low clearingpoint, and a liquid crystal composition with a wide coexistingtemperature range of a nematic phase and an isotropic phase is preparedin a wide temperature range; and then, a chiral reagent is added to theliquid crystal composition.

For a liquid crystal composition with a wide coexisting temperaturerange of a nematic phase or chiral nematic phase and an isotropic phase,the difference between the upper-limit temperature and lower-limittemperature of the co-existence of a chiral nematic phase and anon-liquid crystal isotropic phase is preferably 3-150° C., and morepreferably 5-150° C. Moreover, the liquid crystal composition preferablyhas a difference of 3-150° C. between the upper-limit temperature andlower-limit temperature of the coexistence of a nematic phase and anon-liquid crystal isotropic phase.

When an electric field is applied to the liquid crystal medium of thepresent invention in an optically isotropic liquid crystal phase, anelectric birefringence occurs, but the Kerr effect does not necessarilyoccur.

Because the electric birefringence effect of an optically isotropicliquid crystal phase increases with the pitch, the electricbirefringence effect may be improved by adjusting the type and contentof the chiral reagent to increase the helical pitch, provided that otheroptical properties, such as, transmittance and diffraction wavelength,could be satisfied.

4.4 Other Components

Other compounds, such as polymer material, may be further added into theoptically isotropic liquid crystal composition of the present invention,so long as they do not affect the properties of the composition. Inaddition to the polymer material, the liquid crystal composition of thepresent invention can also contain, for example, a dichroic dye or aphotochromic compound. Examples of the dichroic dye includemerocyanine-based dyes, styryl-based dyes, azo-based dyes,azomethine-based dyes, azoxy-based dyes, quinophthalone-based dyes,anthraquinone-based dyes, tetrazine-based dyes, and the like.

5. Optically Isotropic Polymer/Liquid Crystal Composite Material

A fifth aspect of the present invention is a composite material of apolymer compound and a liquid crystal composition containing thecompound of Formula (1) and a chiral reagent, which exhibits an opticalisotropy. The composite material is an optically isotropicpolymer/liquid crystal composite material which can be used in anoptical device driven in an optically isotropic liquid crystal phase.Such a polymer/liquid crystal composite material is composed of, forexample, the liquid crystal composition according to Items [1]-[33] anda polymer.

The “polymer/liquid crystal composite material” of the present inventionhas no particular limitation, provided that it is a composite containingboth a liquid crystal material and a polymer compound. It also includesa state where the polymer compound and the liquid crystal material arein phase separation because the polymer compound is partially orentirely not dissolved in the liquid crystal material. Furthermore, inthe specification, a nematic phase refers to one, in a narrow sense,excluding a chiral nematic phase, unless specifically indicated.

The optically isotropic polymer/liquid crystal composite materialaccording to a preferred aspect of the present invention can exhibit anoptically isotropic liquid crystal phase in a wide temperature range.Moreover, the polymer/liquid crystal composite material according to apreferred aspect of the present invention has very high response speed.Furthermore, based on such effects, the polymer/liquid crystal compositematerial according to a preferred aspect of the present invention isuseful in an optical device such as a display device.

5.2 Polymers

Although the composite material of the present invention can be producedby mixing an optically isotropic liquid crystal composition with apre-polymerized polymer, it is preferably produced by mixing a lowmolecular weight monomer, macromonomer, or oligomer, etc (generallyreferred to as “monomers”, hereafter) to be formed into a polymermaterial, with the liquid crystal composition (cholesteric liquidcrystal composition), and then polymerizing the mixture. In thespecification, the mixture containing the monomers and the liquidcrystal composition is referred to as “polymerizable monomer/liquidcrystal mixture”. The “polymerizable monomer/liquid crystal mixture” mayoptionally contain a polymerization initiator, a curing agent, acatalyst, a stabilizer, a dichroic dye, or a photochromic compound, andthe like, without compromising the effect of the present invention. Forexample, the polymerizable monomer/liquid crystal mixture of the presentinvention may also optionally contain 0.1-20 weight parts of apolymerization initiator, based on 100 weight parts of the polymerizablemonomer.

The polymerization temperature is preferably such a temperature that thepolymer/liquid crystal composite material exhibits high transparency andisotropy, and more preferably such a temperature that the mixture of themonomer and the liquid crystal material exhibits an isotropic phase or ablue phase, while the polymerization is carried out in the isotropicphase or optically isotropic liquid crystal phase. That is, thetemperature is preferably set, such that after the polymerization, thepolymer/liquid crystal composite material substantially does not scatterlight of wavelength greater than that of visible light and exhibits anoptical isotropy.

For example, a low molecular weight monomer, macromonomer, and oligomermay be used as a raw material of the polymer compound for forming thecomposite material of the present invention. In the specification, theraw material monomers of the polymer compound include low molecularweight monomers, macromonomers, oligomers, and the like. Furthermore,the obtained polymer compound preferably has a three-dimensionalcross-linked structure, and thus the raw material monomer of the polymercompound is preferably a multi-functional monomer having two or morepolymerizable functional groups. The polymerizable functional groupshave no particular limitation, and include, for example, acryloyl,methacryloyl, glycidyl, epoxy, oxetanyl, vinyl, and the like. In view ofthe polymerization rate, acryloyl and methacryloyl are preferred. Theraw material monomers of the polymer compound containing 10 wt % or moreof the monomers having two or more polymerizable functional groups arepreferred, since the obtained composite material of the presentinvention easily exhibits high transparency and isotropy.

Moreover, in order to obtain a better composite material, the polymerpreferably has a mesogen moiety, and a part or all of the raw materialmonomers used have a mesogen moiety.

5.2.1 Mono-functional and Difunctional Monomer Having Mesogen Moiety

The mono-functional or difunctional monomer having a mesogen moiety hasno particular limitation in structure, and may be, for example, thecompounds of Formula (M1) or (M2) below.

In Formula (M1), R^(a) is each independently hydrogen, halogen, —C≡N,—N═C═O, —N═C═S or a C₁₋₂₀ alkyl, in which arbitrary —CH₂ may besubstituted with —O—, —S—, —CO—, —COO—, —OCO—, —CH═CH—, —CF═CF— or—C≡C—, and arbitrary hydrogen in the alkyl and the alkyl with arbitrary—CH₂— substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—, —CF═CF— or —C≡C—may be substituted with halogen or —C≡N. R^(b) is each independently apolymerable group of Formulas (M3-1)-(M3-7).

R^(a) is preferably hydrogen, halogen, —C≡N, —CF₃, —CF₂H, —CFH₂, —OCF₃,—OCF₂H, a C₁₋₂₀ alkyl, a C₁₋₁₉ alkoxy, a C₂₋₂₁ alkenyl, and a C₂₋₂₁alkynyl. Particularly preferably, R^(a) is —C≡N, a C₁₋₂₀ alkyl, and aC₁₋₁₉ alkoxy.

In Formula (M2), R^(b) is each independently a polymerable group ofFormulas (M3-1)-(M3-7).

Herein, in Formulas (M3-1)-(M3-7), R^(d) is each independently hydrogen,halogen, or a C₁₋₅ alkyl, in which arbitrary hydrogen may be substitutedwith halogen. R^(d) is preferably hydrogen, halogen, and methyl.Particularly preferably, R^(d) is hydrogen, fluorine, and methyl.

Furthermore, Formulas (M3-2), (M3-3), (M3-4), and (M3-7) are preferablypolymerized through free radical polymerization. Formulas (M3-1),(M3-5), and (M3-6) are preferably polymerized through cationicpolymerization. The polymerizations are both living polymerization, andthus can be initiated only when a small amount of free radical orcationic active species is generated in the reaction system. In order toaccelerate the generation of the active species, a polymerizationinitiator may be used. Light or heat may be used to generate the activespecies.

In Formulas (M1) and (M2), A^(M) is each independently an aromatic ornon-aromatic 5- or 6-membered ring, or a fused ring having 9 or morecarbon atoms, in which —CH₂— in the rings may be substituted with —O—,—S—, —NH—, or —NCH₃—, —CH═ in the rings may be substituted with —N═, andhydrogen atom in the rings may be substituted with halogen, and a C₁₋₅alkyl or haloalkyl. Specific examples of preferred A^(M) are1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene,naphthalene-2,6-diyl, tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl,or bicyclo[2.2.2]octane-1,4-diyl, in which arbitrary —CH₂— in the ringsmay be substituted with —O—, arbitrary —CH═ may be substituted with —N═,and arbitrary hydrogen in the rings and the rings with arbitrary —CH═substituted with —CH═ may be substituted with halogen, a C₁₋₅ alkyl, ora C₁₋₅ haloalkyl.

In consideration of the stability of the compound, —CH₂—O—CH₂—O— withoxygen being not adjacent to one another is preferred to —CH₂—O—O—CH₂—with oxygen being adjacent to one another. This also applies to the caseof sulphur.

Among the groups, especially preferred A^(M) is 1,4-cyclohexylene,1,4-cyclohexenylene, 1,4-phenylene, 2-fluoro-1,4-phenylene,2,3-difluoro-1,4-phenylene, 2,5-difluoro-1,4-phenylene,2,6-difluoro-1,4-phenylene, 2-methyl-1,4-phenylene,2-trifluoromethyl-1,4-phenylene, 2,3-bis(trifluoromethyl)-1,4-phenylene,naphthalene-2,6-diyl, tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl,9-methylfluorene-2,7-diyl, 1,3-dioxane-2,5-diyl, pyridine-2,5-diyl, andpyrimidine-2,5-diyl. Moreover, as for the stereo configuration of1,4-cyclohexylene and 1,3-dioxane-2,5-diyl, trans-configuration issuperior to cis-configuration.

Because 2-fluoro-1,4-phenylene and 3-fluoro-1,4-phenylene are identicalin structure, the latter is not exemplified. This also applies to thecase of the relationship between 2,5-difluoro-1,4-phenylene and3,6-difluoro-1,4-phenylene.

In Formulas (M1) and (M2), Y is each independently a single bond, or aC₁₋₂₀ alkylene, in which arbitrary —CH₂— may be substituted with —O—,—S—, —CH═CH—, —C≡C—, —COO— or —OCO—. Y is preferably a single bond,—(CH₂)_(m2)—, —O(CH₂)_(m2)—, and —(CH₂)_(m2)O— (where m2 is an integerof 1-20). Particularly preferably, Y is a single bond, —(CH₂)_(m2)—,—O(CH₂)_(m2)—, and —(CH₂)_(m2)O— (where m2 is an integer of 1-10). Inconsideration of the stability of the compound, —Y—R^(a) and —Y—R^(b)preferably have no —O—O—, —O—S—, —S—O—, or —S—S—.

In Formulas (M1) and (M2), Z^(M) is each independently a single bond,—(CH₂)_(m3)—, —O(CH₂)_(m3)—, —(CH₂)_(m3)O—, —O(CH₂)_(m3)O—, —CH═CH—,—C≡C—, —COO—, —OCO—, —(CF₂)₂—, —(CH₂)₂—COO—, —OCO—(CH₂)₂—, —CH═CH—COO—,—OCO—CH═CH—, —C≡C—COO—, —OCO—C≡C—, —CH═CH—(CH₂)₂—, —(CH₂)₂—CH═CH—,—CF═CF—, —C≡C—CH═CH—, —CH═CH—C≡C—, —OCF₂—(CH₂)₂—, —(CH₂)₂—CF₂O—, —OCF₂—,or —CF₂O—(where m3 is an integer of 1-20).

Z^(M) is preferably a single bond, —(CH₂)_(m3)—, —O(CH₂)_(m3)—,—(CH₂)_(m3)O—, —CH═CH—, —C≡C—, —COO—, —OCO—, —(CH₂)₂—COO—, —OCO—(CH₂)₂—,—CH═CH—COO—, —OCO—CH═CH—, —OCF₂—, and —CF₂O—.

In Formulas (M1) and (M2), m1 is an integer of 1-6, and preferably aninteger of 1-3. When m1 is 1, the compound is a bicyclic compound havingtwo, for example, 6-membered rings. When m1 is 2 or 3, the compound is atricyclic or tetracyclic compound, respectively. For example, when m1 is1, two A^(M) may be identical or different. Furthermore, for examplewhen m1 is 2, three A^(M) (or two Z^(M)) may be identical or different.When m1 is 3-6, it is also the same case. This also applies to the caseof R^(a), R^(b), R^(d), Z^(M), A^(M), and Y.

Even the Compound (M1) of Formula (M1) and the Compound (M2) of Formula(M2) contains an isotope in an amount higher than its natural abundance,such as ²H (deuterium) and ¹³C are useful, due to the identicalproperties.

More preferred examples of Compounds (M1) and (M2) are Compounds(M1-1)-(M1-41) and (M2-1)-(M2-27) of Formulas (M1-1)-(M1-41) and(M2-1)-(M2-27). Among the compounds, R^(a), R^(b), R^(d), Z^(M), A^(M),Y, and p have the same meaning as those described for Formulas (M1) and(M2) in the previous aspects of the present invention.

Each partial structure of Compounds (M1-1)-(M1-41) and Compounds(M2-1)-(M2-27) is described as follows. Partial structure (a1)represents 1,4-phenylene with arbitrary hydrogen substituted withfluorine. Partial structure (a2) represents 1,4-phenylene in whicharbitrary hydrogen may be substituted with fluorine. Partial structure(a3) represents 1,4-phenylene in which arbitrary hydrogen may besubstituted with either fluorine or methyl. Partial structure (a4)represents fluorene in which hydrogen at position 9 may be substitutedwith methyl.

A polymerizable compound other than the monomer having no mesogen moietyand the monomers (M1) and (M2) having mesogen moiety may be used, ifdesired.

In order to optimize the optical isotropy of the polymer/liquid crystalcomposite material of the present invention, a monomer having a mesogenmoiety and three or more polymerizable functional groups can also beused. The monomer having a mesogen moiety and three or morepolymerizable functional groups is preferably a well-know compound, forexample, (M4-1)-(M4-3), and more specifically, the compounds describedin Japanese Patent Publication Nos. 2000-327632, 2004-182949, and2004-59772. In (M4-1)-(M4-3), R^(b), Z^(M), Y, and (F) have the samemeaning as described above.

5.2.2 Monomer Having No Mesogen Moiety and Having PolmerizableFunctional Group

Examples of the monomer having no mesogen moiety and having apolymerizable group are linear or branched acrylate of 1-30 carbons,linear or branched diacrylate of 1-30 carbons, and a monomer havingthree or more polymerizable groups, for example, but not limited to,glycerol-propoxide (1PO/OH) triacrylate, pentaerythritol-propoxidetriacrylate, pentaerythritol triacrylate, trimethylolpropane-ethoxidetriacrylate, trimethylolpropane-propoxide triacrylate,trimethylolpropane triacrylate, di(trimethylolpropane)tetraacrylate,pentaerythritol tetraacrylate, di(pentaerythritol)pentaacrylate,di(pentaerythritol)hexaacrylate, and trimethylolpropane triacrylate.

5.2.3 Polymerization Initiator

The polymerization pattern used to produce the polymer compound forforming the composite material of the present invention has noparticular limitation, and may be, for example, photo-radicalpolymerization, thermo-radical polymerization, and photo-cationicpolymerization.

The photo-radical polymerization initiator useful for photo-radicalpolymerization is, for example, DAROCUR™ 1173 and DAROCUR 4265 (both aretrade names, from Ciba Specialty Chemicals), IRGACURE™ 184, IRGACURE369, IRGACURE 500, IRGACURE 651, IRGACURE 784, IRGACURE 819, IRGACURE907, IRGACURE 1300, IRGACURE 1700, IRGACURE 1800, IRGACURE 1850, andIRGACURE 2959 (all are trade names, from Ciba Specialty Chemicals).

Preferred examples of the thermo-radical polymerization initiatorsuseful for thermo-radical polymerization are benzoyl peroxide,diisopropyl peroxydicarbonate, tert-butyl peroxy(2-ethylhexanoate),tert-butyl peroxypivalate, tert-butyl peroxydiisobutyrate, lauroylperoxide, dimethyl 2,2′-azobisisobutyrate (MAIB), di-t-butyl peroxide(DTBPO), azobisisobutyronitrile (AIBN), andazobiscyclohexanecarbonitrile (ACN), and the like.

Examples of the photo-cationic polymerization initiator useful forphoto-cationic polymerization are diaryliodonium salt (referred to as“DAS”, hereafter), and triarylsulfonium salt (referred to as “TAS”,hereafter), and the like.

Examples of DAS are diphenyliodonium tetrafluoroborate, diphenyliodoniumhexafluorophosphate, diphenyliodonium hexafluoroarsenate,diphenyliodonium trifluoromesylate, diphenyliodonium trifluoroacetate,diphenyliodonium p-toluenesulfonate, diphenyliodoniumtetrakis(pentafluorophenyl)borate, 4-methoxyphenylphenyliodoniumtetrafluoroborate, 4-methoxyphenylphenyliodonium hexafluorophosphate,4-methoxyphenylphenyliodonium hexafluoroarsenate,4-methoxyphenylphenyliodonium trifluoromesylate,4-methoxyphenylphenyliodonium trifluoroacetate, and4-methoxyphenylphenyliodonium p-toluenesulfonate.

DAS may be sensitized by adding a photosensitizer, such as thioxanthone,phenothiazine, chlorothioxanthone, xanthone, anthracene, diphenylanthracene, and rubrene.

Examples of TAS are triphenylsulfonium tetrafluoroborate,triphenylsulfonium hexafluorophosphate, triphenylsulfoniumhexafluoroarsenate, triphenylsulfonium trifluoromesylate,triphenylsulfonium trifluoroacetate, triphenylsulfoniump-toluenesulfonate, triphenylsulfoniumtetrakis(pentafluorophenyl)borate, 4-methoxyphenyldiphenylsulfoniumtetrafluoroborate, 4-methoxy phenyldiphenylsulfoniumhexafluorophosphate, 4-methoxyphenyldiphenylsulfoniumhexafluoroarsenate, 4-methoxyphenyldiphenylsulfonium trifluoromesylate,4-methoxyphenyldiphenylsulfonium trifluoroacetate, and4-methoxyphenyldiphenylsulfonium p-toluenesulfonate, and the like.

Specific examples of the photo-cationic polymerization initiator areCyracure™ UVI-6990, Cyracure UVI-6974, and Cyracure UVI-6992 (all aretrade names, from UCC Corporation); Adeka Optomer SP-150, Adeka OptomerSP-152, Adeka Optomer SP-170, Adeka Optomer SP-172 (all are trade names,from ADEKA Corporation), Rhodorsil Photoinitiator 2074 (trade name, fromRHODIA JAPAN Corporation), IRGACURE™ 250 (trade name, from CibaSpecialty Chemicals), and UV-9380C (trade name, from GE TOSHIBASILICONES Co. Ltd), and the like.

5.2.4 Curing Agents and Others

In preparing the polymer compound for forming the composite material ofthe present invention, in addition to the monomers and thepolymerization initiator above, one or two or more other preferredcomponents, such as, curing agent, catalyst, and stabilizer, may also befurther added.

The latent curing agents well-known in the art which are commonly usedas curing agent for epoxy resins may be used. Examples of the latentcuring agent for epoxy resins are amine-based curing agents, novolacresin-based curing agents, imidazole-based curing agents, andanhydride-based curing agents, and the like. Examples of amine-basedcuring agents are aliphatic polyamines such as diethylenetriamine,triethylenetetraamine, tetraethylenepentaamine, m-xylenediamine,trimethyl hexamethylenediamine, 2-methyl pentamethylenediamine, anddiethylaminopropylamine; alicyclic polyamines such as isophoronediamine, 1,3-diaminomethylcyclohexane, bis(4-aminocyclohexyl)methane,norbornanediamine, 1,2-diaminocyclohexane, and Laromin; and aromaticpolyamines such as diaminodiphenylmethane, diaminodiphenylethane, andm-phenylenediamine.

Examples of novolac-based curing agents are phenolic novolac resin, andbisphenolic novolac resin, and the like. Examples of imidazole-basedcuring agents are 2-methylimidazole, 2-ethylhexylimidazole,2-phenylimidazole, and 1-cyanoethyl-2-phenylimidazolium trimellitate,and the like.

Examples of anhydride-based curing agents are tetrahydrophthalicanhydride, hexahydrophthalic anhydride, methyltetrahydrophthalicanhydride, methylhexahydrophthalic anhydride, methylcyclohexenetetracarboxylic dianhydride, phthalic anhydride, trimellitic anhydride,pyromellitic dianhydride, and benzophenone tetracarboxylic dianhydride,and the like.

Furthermore, a curing accelerator may further be used to facilitate thecuring reaction of a polymerizable compound with glycidyl, epoxy, oroxetanyl and the curing agent. Examples of the curing accelerator aretertiary amines such as benzyldimethylamine,tris(dimethylaminomethyl)phenol, and dimethylcyclohexylamine; imidazolessuch as 1-cyanoethyl-2-ethyl-4-methylimidazole, and2-ethyl-4-methylimidazole; organophosphorus compounds such astriphenylphosphine; quaternary phosphosium salts such astetraphenylphosphosium bromide; diazobicyclo alkenes such as1,8-diazobicyclo[5.4.0]undecene-7 or an organic acid salt thereof;quaternary ammonium salts such as tetraethylammonium bromide, andtetrabutylammonium bromide; boron compounds such as boron trifluoride,and triphenyl borate, and the like. These curing accelerators may beused alone, or in a combination of two or more.

Moreover, a stabilizer is preferably added, for example, to preventunwanted polymerization during storage. The stabilizer may be anycompound well known to those of ordinary skill in the art,representative examples of which are 4-ethoxyphenol, hydroquinone, andbutylated hydroxytoluene (BHT), and the like.

5.3 Content of Liquid Crystal Composition

The content of the liquid crystal composition in the polymer/liquidcrystal composite material of the present invention is preferably ashigh as possible, so long as it is within a range in which the compositematerial exhibits an optically isotropic liquid crystal phase. Thereason lies in the fact that the higher the content of the liquidcrystal composition is, the greater the electric birefringence value ofthe composite material of the present invention is.

In the polymer/liquid crystal composite material of the presentinvention, the content of the liquid crystal composition is preferably60-99 wt %, more preferably 60-95 wt %, and particularly preferably65-95 wt %, with respect to the composite material. The content of thepolymer is preferably 1-40 wt %, more preferably 5-40 wt %, andparticularly preferably 5-35 wt %, with respect to the compositematerial.

5.4 Other Components

The polymer/liquid crystal composite material of the present inventionmay also contain, for example, a dichroic dye and a photochromiccompound, without prejudice to the effect of the present invention.

The present invention is further described in detail with reference toexamples; however, the present invention is not limited to thereto.Furthermore, “%” denotes “wt %”, unless specifically indicated.

6 Optical Device

A sixth aspect of the present invention is an optical device, whichcontains the liquid crystal composition or the polymer/liquid crystalcomposite material (hereafter, both are sometimes collectively referredto as liquid crystal medium) and is driven in an optically isotropicliquid crystal phase.

The liquid crystal medium is optically isotropic in the absence of anelectric field and exhibits an optical anisotropy in the presence of anelectric field, such that optical modulation may be achieved with anelectric field.

As an example of the structure of the LCD device, as shown in FIG. 1,the electrodes on the comb-like electrode substrate have such astructure that Electrode 1 extending from the left side and Electrode 2extending from the right side are alternatively arranged. When apotential difference exists between Electrode 1 and Electrode 2, thecomb-like electrode substrate is provided with an electric field in twodirections (upward and downward), as shown in FIG. 1.

EXAMPLES

The resulting compound is characterized by a nuclear magnetic resonance(NMR) spectrum obtained by ¹H-NMR analysis and a gas chromatogramobtained by gas chromatography (GC) analysis. The analysis methods arefirstly illustrated below.

¹H-NMR analysis: ¹H-NMR analysis was carried out by using DRX-500(manufactured by Bruker BioSpin Co., Ltd). In the measurement, a sampleprepared in an embodiment was dissolved in a deuterated solvent, such asCDCl₃, which is capable of dissolving the sample, and then was measuredwith a NMR apparatus at 500 MHz at room temperature in 24 times ofaccumulation. In the resulting NMR spectrum, s denotes singlet, ddenotes doublet, t denotes triplet, q denotes quartet, and m denotesmultiplet. Furthermore, tetramethylsilane (TMS) was used as the standardof chemical shift δ of zero.

GC analysis: GC analysis was carried out by using a GC apparatus ModelGC-14B (manufactured by Shimazu). The column was the capillary columnCBP1-M25-025 (length 25=m, inner diameter=0.22 mm, film thickness=0.25μm, manufactured by Shimazu); and the stationary liquid phase waspolydimethylsiloxane (non-polarity). The carrier gas was helium, and theflow rate was adjusted to 1 ml/min. The sample evaporation chamber wasset at 300° C., and the detector (flame ionization detector, FID) wasset at 300° C.

A sample was dissolved in toluene to give a solution of 1 wt %, and then1 μl of the solution was injected into the sample evaporation chamber.

The recorder used was Chromatopac Model C-R6A (manufactured by Shimazu)or an equivalent thereof. The obtained gas chromatogram exhibited peakretention times and peak areas corresponding to the component compounds.

In addition, the solvent for diluting the sample was, for example,chloroform or hexane. The column used was, for example, capillary columnDB-1 (length=30 m, inner diameter=0.32 mm, film thickness=0.25 m,manufactured by Agilent Technologies Inc.), HP-1 (length=30 m, innerdiameter=0.32 mm, film thickness=0.25 μm., manufactured by AgilentTechnologies Inc.), Rtx-1 (length=30 m, inner diameter=0.32 mm, filmthickness=0.25 μm, manufactured by Restek Corporation), or BP-1(length=30 m, inner diameter=0.32 mm, film thickness=0.25 μm,manufactured by SGE International Pty. Ltd.).

The area ratios of the peaks in the gas chromatogram correspond to theratios of the component compounds. Generally, the weight percentages ofthe component compounds in the analyzed sample are not completelyidentical to the area percentages of the peaks. However, in the presentinvention, when the columns described above are used, the correctioncoefficient is substantially 1. Therefore, the weight percentages of thecomponent compounds in the analyzed sample are substantiallycorresponding to the area percentages of the peaks. The reason lies inthat there is no significant difference among the correctioncoefficients of the component compounds. In order to more accuratelycalculate the ratios of the liquid crystal compounds in the liquidcrystal composition with GC, the internal standard method for GC may beused. GC measurements were simultaneously performed on an accuratelyweighed specified amount of a liquid crystal compound component(detected component) and a liquid crystal compound as standard(standard), and the relative intensity was previously calculated as peakarea ratio of the detected component to the standard. If a correctionwas performed by using the relative intensity expressed as peak arearatio of each component to the standard, the ratios of the liquidcrystal compounds in the liquid crystal composition can be moreaccurately calculated with GC analysis.

Samples for Determining Characteristic Values of Liquid CrystalCompounds

Two methods may be used to measure the characteristic values of a liquidcrystal compound, i.e., taking a pure compound as a sample, and mixing acompound in a mother liquid crystal to form a sample.

When a sample prepared by mixing a compound with a mother liquid crystalis used, the following method is used for the measurement. Firstly, 15wt % of the resulting liquid crystal compound was mixed with 85 wt % ofthe mother liquid crystal to prepare a sample, and then an extrapolatedvalue is calculated from the measured value of the sample according tothe extrapolation method based on the equation below, as thecharacteristic value of the compound.[Extrapolated Value]=(100×[measured value of the sample]−[wt % of themother liquid crystal]×[measured value of the mother liquidcrystal])/[wt % of the liquid crystal compound]

While a smectic phase or crystal may be precipitated at the above ratioof the liquid crystal compound and the mother liquid crystal at 25° C.,the ratio of the liquid crystal compound and the mother liquid crystalis changed to be 10 wt %:90 wt %, 5 wt %:95 wt %, 1 wt %:99 wt % inorder. The composition without separation of a smectic phase or crystalat 25° C. was measured for the characteristic value of the samples, andthe characteristic values of the liquid crystal compound is calculatedthrough extrapolation based on above equation.

There are numerous mother liquid crystals that may be used for themeasurement. For example, the composition of the mother liquid crystal Ais as follows (wt %).

Mother Liquid Crystal A:

Method for Measuring Characteristic Values of Liquid Crystal Compounds

The measurement of the characteristic values was carried out with themethods below. These methods are mainly those described inEIAJ•ED-12521A of the Standard of Electric Industries Association ofJapan, or modifications of the same. Moreover, the TN device used in themeasurement was not equipped with TFT.

With respect to the determined values, in case that the liquid crystalcompound itself is used as a sample, the obtained values are recorded asexperimental data; and in case that a mixture of the liquid crystalcompound and a mother liquid crystal is used as a sample, theextrapolated values obtained with the extrapolation method are recordedas experimental data.

The phase structure and the phase transition temperature (° C.) weremeasured by using the methods (1) and (2) below.

(1) A compound was placed on a hot plate (Hot Stage, Model FP-52,manufactured by Mettler, Corp.) in a melting point measuring apparatusequipped with a polarizing microscope, and the phase behaviour and itschange were observed by the polarizing microscope while the sample washeated at a rate of 3° C./min, to determine the type of the liquidcrystal phase.

(2) A scanning calorimetry DSC-7 system or Diamond DSC system(manufactured by PerkinElmer Corp.) was used, at a heating or coolingrate of 3° C./min, and the on set of the endothermic peak or theexothermic peak along with the phase change of the sample was calculatedwith the extrapolation method, to determine the phase transitiontemperature.

Hereafter, a crystal is represented by K, and for differentiation, twocrystals are represented by K₁ or K₂, respectively. A smectic phase isrepresented by Sm, a nematic phase is represented by N, and a liquid(isotropic phase) is represented by I. For differentiation, a smectic Bphase and a smectic A phase in the smectic phase are represented by SmBand SmA, respectively. BP represents a blue phase or an opticallyisotropic liquid crystal phase. A biphase coexistence is sometimesrepresented by (N*+I) or (N*+BP). Specifically, (N*+I) represents aphase in which a non-liquid crystal isotropic phase and a chiral nematicphase coexist, and (N*+BP) represents a phase in which a BP phase or anoptically isotropic liquid crystal phase and a chiral nematic phasecoexist. Un represents a non-optically isotropic unidentified phase. Forthe expression of the phase transition temperature, for example, “K 50.0N 100.0 I” means that the phase transition temperature (KN) from thecrystal to the nematic phase is 50.0° C., and the phase transitiontemperature (NI) from the nematic phase to the liquid is 100.0° C. Thisalso applies to the case of other expressions.

Upper-limit temperature of a nematic phase (T_(NI), ° C.): a sample (amixture of a liquid crystal compound and a mother liquid crystal) wasplaced on a hot plate (Hot Stage, Model FP-52, manufactured by MettlerCorp.) in a melting point measuring apparatus equipped with a polarizingmicroscope, and was observed with the polarizing microscope while thesample was heated at a rate of 1° C./min. The temperature at which apart of the sample began to change from a nematic phase into anisotropic liquid was recorded as the upper-limit temperature of thenematic phase, sometimes abbreviated as “upper-limit temperature”hereafter.

Low-temperature compatibility: samples were prepared by mixing a motherliquid crystal with a liquid crystal compound in such a manner that thecontent of the latter was 20 wt %, 15 wt %, 10 wt %, 5 wt %, 3 wt %, and1 wt %, respectively, and then placed into glass bottles. The glassbottles were kept in a freezer at −10° C. or −20° C. for a specifiedperiod of time, and the presence or absence of a crystal or a smecticphase was observed.

Viscosity (η, determined at 20° C., mPa·s): the viscosity of a mixtureof a liquid crystal compound and a mother liquid crystal is measuredwith an E-type rotational viscometer.

Refractive index anisotropy (Δn): the measurement was carried out at 25°C. by using light having a wavelength of 589 nm, with an Abberefractometer having a polarizing plate mounted on an ocular lens. Afterthe surface of the main prism is rubbed in a direction, a sample (amixture of a liquid crystal compound and a mother liquid crystal) wasdripped onto the main prism. The refractive index (n_(//)) wasdetermined when the polarizing direction was paralleled to the rubbingdirection, and the refractive index (n_(⊥)) was determined when thepolarizing direction was perpendicular to the rubbing direction. Thevalue of refractive index anisotropy (Δn) was calculated according tothe equation Δn=n_(//)−n_(⊥).

Dielectric anisotropy (Δ∈: determined at 25° C.): a sample (a mixture ofa liquid crystal compound and a mother liquid crystal) was fed into aliquid crystal cell with a distance (cell gap) of about 9 μm between twoglass substrates and a twist angle of 80 degrees. The liquid crystalcell was applied with a voltage of 20 V and the dielectric constant(∈_(//)) in the major-axis direction of the liquid crystal molecule wasdetermined. Then, a voltage of 0.5 V was applied and the dielectricconstant (∈_(⊥)) in the minor axis direction of the liquid crystalmolecule was determined. The value of dielectric anisotropy wascalculated according to the equation Δ∈=∈_(//)−∈_(⊥).

Pitch (P; Determined at 25° C., m)

A pitch length was measured through selective reflection (Handbook ofLiquid Crystal, p 196, 2000, Maruzen). For the selective reflectionwavelength λ, the relationship <n>p/λ=1 exists. Here, <n> denotes theaverage refractive index, and is calculated according to the equation<n>={(n_(//) ²+n_(⊥) ²)/2}^(1/2). The selective reflection wavelengthwas determined by a microspectrophotometer (Trade name MSV-350,manufactured by Japan Electronics Co., Ltd.). The pitch was calculatedby dividing the resulting reflection wavelength by the averagerefractive index. When the concentration of the optically activecompound is low, the pitch of a cholesteric liquid crystal having areflection wavelength in a region of wavelength longer than that ofvisible light is proportional to the reciprocal of the concentration.Therefore, multiple points were measured for the pitch length of theliquid crystal having a selective reflection wavelength in the visiblelight region, and then the pitch was calculated by using a linearextrapolation method. The “optically active compound” is equivalent tothe chiral reagent in the present invention.

Synthesis Example 1

Synthesis of Formula (S1-8)

The synthesis scheme is as shown below.

Synthesis of Compound (S1-2)

88.3 g (S1-1), 7.54 g catalyst, and 900 ml tetrahydrofuran (THF) werecharged into a reactor under a nitrogen atmosphere, and 2 mol/L solutionof butylmagnesium chloride in THF was added dropwise at roomtemperature, and refluxed for 4 h. The reaction solution was cooled toroom temperature, which was added with toluene, and then washed with 1 Nhydrochloric acid and water. After drying over magnesium sulfate, thesolvent was removed under vacuum. After chromatography on silica gelcolumn with heptane as a developing solvent, and drying under vacuum,75.7 g (S1-2) was obtained. The yield of (S1-2) obtained from (S1-1) is93.1%.

Synthesis of Compound (S1-3)

55.5 g (S1-2) and 550 ml THF were charged into a reactor under anitrogen atmosphere, and cooled to −70° C., and then 161 ml n-BuLi (1.55M; solution in n-hexane) was added dropwise and stirred for 1 hr at −70°C. 450 ml solution of 63.4 g iodine in THF was added dropwise to thereaction solution at −70° C., and stirred for 5 h. The reaction solutionwas warmed to room temperature, and then poured into a solution ofsodium thiosulfate in water. The product was extracted with ethylacetate, and then the organic layer was washed with an aqueous sodiumthiosulfate solution and water. After drying over magnesium sulfate, thesolvent was removed through distillation under vacuum. Afterchromatography on silica gel column with heptane/toluene=3/1 as adeveloping solvent, and drying under vacuum, 79.1 g (S1-3) was obtained.The yield of (S1-3) obtained from (S1-2) is 97.5%.

Synthesis of Compound (S1-5)

79.1 g (S1-3), 38.4 g 3,5-difluorophenylboronic acid (S1-4), 3.5 gtetrakis(triphenylphosphine)palladium, 70.9 g sodium carbonate, and 560ml mixed solvent of toluene/ethanol/water=3/3/1 (volume ratio) werecharged into a reactor under a nitrogen atmosphere, and refluxed for 7h. The reaction solution was cooled to room temperature, which was addedwith toluene, and then washed with 1 N hydrochloric acid and water.After drying over magnesium sulfate, the solvent was removed throughdistillation under vacuum. After chromatography on silica gel columnwith heptane as a developing solvent, drying under vacuum, andrecrystallization of the remaining component in a mixed solvent ofethanol/ethyl acetate=4/1, 50.6 g (S1-5) was obtained. The yield of(S1-5) obtained from (S1-3) is 66.2%.

Synthesis of Compound (S1-6)

15.0 g Compound (S1-5) and 150 ml THF were charged into a reactor undera nitrogen atmosphere, and then cooled to −74° C. 27.4 ml 1.60 M n-butyllithium solution in n-hexane was added dropwise at a temperature in arange of −74° C. to −60° C., and then further stirred for 60 min. Then,20.0 ml solution of 12.6 g dibromodifluoromethane in THF was addeddropwise at a temperature in a range of −75° C. to −70°, warmed back to25° C., and stirred for 60 min. The resulting reaction mixture waspoured into 150 ml ice water, and mixed. 100 ml toluene was added, toform an organic layer and an aqueous layer separated from each other,and the resulting organic layer was obtained through extraction, whichwas washed with brine, and dried over anhydrous magnesium sulfate. Theresulting solution was concentrated under vacuum, and the residue waspurified by chromatography on silica gel column with heptane as adeveloping solvent. After removal of the solvent through distillation,and drying, 16.5 g (S1-6) was obtained.

Synthesis of Compound (S1-8)

6.0 g Compound (S1-6), 1.4 g 3,4,5-trifluorophenol (S1-7), 2.8 gpotassium carbonate, 100 ml N,N-dimethylformamide (DMF) were chargedinto a reactor under a nitrogen atmosphere, and stirred for 120 min at90° C. After the temperature of the reaction mixture was returned backto 25° C., the reaction mixture was then poured into 50 ml ice water andmixed. 100 ml toluene was added, to form an organic layer and an aqueouslayer separated from each other, and the resulting organic layer wasobtained through extraction, which was then washed with a saturatedaqueous sodium bicarbonate solution, 0.5 N aqueous sodium hydroxidesolution, and saline in sequence, and dried over anhydrous magnesiumsulfate. The resulting solution was concentrated under vacuum, and theresidue was purified by chromatography on silica gel column with heptaneas a developing solvent. Then, after purification throughrecrystallization in a mixed solvent of heptane/Solmix A-11 and drying,1.7 g (S1-8) was obtained. The yield of (S1-8) obtained from (S1-5) is20.4%.

The phase transition temperature of the resulting Compound (S1-8) is asfollows.

Phase transition temperature (° C.): K 92.4 N 95.4 I.

The resulting compound was identified to be (S1-9) through the followingchemical shift δ (ppm) obtained with ¹H-NMR analysis using CDCL₃ assolvent. Chemical shift δ (ppm): 7.36 (t, 1H), 7.26-7.20 (m, 4H), 7.08(d, 1H), 7.04-6.99 (m, 3H), 2.67 (t, 2H), 1.67-1.64 (m, 2H), 1.41-1.37(m, 2H), 0.96 (t, 3H).

Physical Properties of Liquid Crystal Compound (S1-8)

The four compounds designated as mother liquid crystal A above weremixed, to prepare a mother liquid crystal A having a nematic phase. Thephysical properties of the mother liquid crystal A are as follows.

Upper-limit temperature (T_(NI))=71.7° C.; dielectric anisotropy(Δ∈)=11.0; and refractive index anisotropy (Δn)=0.137.

Liquid Crystal Composition B containing 90 wt % of the mother liquidcrystal A and 10 wt % of (S1-8) obtained in Synthesis Example 1 wasprepared. The characteristic values of the resultant Liquid CrystalComposition B were determined. The extrapolated characteristic values ofLiquid Crystal Compound (S1-8) calculated based on the measurementsthrough extrapolation are as follows.

Upper-limit temperature (T_(NI))=54.7° C.; dielectric anisotropy(Δ∈)=54.2; and refractive index anisotropy (Δn)=0.167.

It can be known from the results that, Liquid Crystal Compound (S1-8)has a large dielectric anisotropy (Δ∈), and refractive index anisotropy(Δn).

Synthesis Examples 2-4

Synthesis of (S2-1), (S3-1), and (S4-1)

The unit of the phase transition temperature is ° C.

Synthesis of Compounds (S2-1), (S3-1), and (S4-1)

The compounds are synthesized with suitable reagents following themethod of Synthesis Example 1.

Physical Properties of Liquid Crystal Compound (S2-1)

The four compounds designated as mother liquid crystal A above weremixed, to prepare a mother liquid crystal A having a nematic phase. Thephysical properties of the mother liquid crystal A are as follows.

Upper-limit temperature (T_(NI))=71.7° C.; dielectric anisotropy(Δ∈)=11.0; and refractive index anisotropy (Δn)=0.137.

Liquid Crystal Composition C containing 90 wt % of the mother liquidcrystal A and 10 wt % of (S2-1) obtained in Synthesis Example 2 wasprepared. The characteristic values of the resultant Liquid CrystalComposition C were determined. The extrapolated characteristic values ofthe Liquid Crystal Compound (S2-1) calculated based on the measurementsthrough extrapolation are as follows.

Upper-limit temperature (T_(NI))=61.7° C.; dielectric anisotropy(Δ∈)=51.1; and refractive index anisotropy (Δn)=0.177.

It can be known from the results that Liquid Crystal Compound (S2-1) hasa large dielectric anisotropy (Δ∈) and refractive index anisotropy (Δn).

Physical Properties of Liquid Crystal Compound (S3-1)

Liquid Crystal Composition D containing 95 wt % of the mother liquidcrystal A and 5 wt % of (S3-1) obtained in Synthesis Example 2 wasprepared. The characteristic values of the resultant Liquid CrystalComposition C were determined. The extrapolated characteristic values ofLiquid Crystal Compound (S3-1) calculated based on the measurementsthrough extrapolation are as follows.

Upper-limit temperature (T_(NI))=55.7° C.; dielectric anisotropy(Δ∈)=68.1; and refractive index anisotropy (Δn)=0.177.

It can be known from the results that Liquid Crystal Compound (S3-1) hasa very large dielectric anisotropy (Δ∈).

Physical Properties of Liquid Crystal Compound (S4-1)

Liquid Crystal Composition E containing 90 wt % of the mother liquidcrystal A and 10 wt % of (S4-1) obtained in Synthesis Example 2 wasprepared. The characteristic values of the resultant Liquid CrystalComposition E were determined. The extrapolated characteristic values ofthe Liquid Crystal Compound (S4-1) calculated based on the measurementsthrough extrapolation are as follows.

Upper-limit temperature (T_(NI))=59.7° C.; dielectric anisotropy(Δ∈)=65.9; and refractive index anisotropy (Δn)=0.167.

It can be known from the results that Liquid Crystal Compound (S4-1) hasa very large dielectric anisotropy (Δ∈).

Synthesis Example 5

Synthesis of (S5-3)

The synthesis scheme is as shown below.

Synthesis of Compound (S5-3)

Synthesis of (S5-1) from (S1-2) is achieved following the method forsynthesizing (S1-6) from (S1-5) in Synthesis Example 1, in which (S1-2)is used in place of (S1-5). Synthesis of (S5-3) from (S5-1) is achievedfollowing the method for synthesizing (S1-8) from (S1-6) in SynthesisExample 1, in which (S5-1) is used in place of (S1-6), and (S5-2) isused in place of (S1-7). The phase transition temperature of theresultant compound (S5-3) is as follows.

Phase transition temperature (° C.): K 63.1N 88.5 I.

Physical Properties of Liquid Crystal Compound (S5-3)

Liquid Crystal Composition F containing 85 wt % of the mother liquidcrystal A and 15 wt % of (S5-3) obtained in Synthesis Example 5 wasprepared. The characteristic values of the resultant Liquid CrystalComposition F were determined. The extrapolated characteristic values ofthe Liquid Crystal Compound (S5-3) calculated based on the measurementsthrough extrapolation are as follows.

Upper-limit temperature (T_(NI))=55.7° C.; dielectric anisotropy(Δ∈)=42.1; and refractive index anisotropy (Δn)=0.164.

It can be known from the results that Liquid Crystal Compound (S5-3) hasgood compatibility with other liquid crystal compounds, and has a largedielectric anisotropy (Δ∈), and refractive index anisotropy (Δn).

Synthesis Example 6

Synthesis of (S6-1)

Synthesis of Compound (S6-1)

(S6-1) is synthesized following the method for synthesizing (S5-3) inSynthesis Example 5.

Physical Properties of Liquid Crystal Compound (S6-1)

Liquid Crystal Composition G containing 85 wt % of the mother liquidcrystal A and 15 wt % of (S6-1) obtained in Synthesis Example 6 wasprepared. The characteristic values of the resultant Liquid CrystalComposition G were determined. The extrapolated characteristic values ofthe Liquid Crystal Compound (S6-2) calculated based on the measurementsthrough extrapolation are as follows.

Upper-limit temperature (T_(NI))=51.0° C.; dielectric anisotropy(Δ∈)=43.4; and refractive index anisotropy (Δn)=0.164.

It can be known from the results that Liquid Crystal Compound (S6-1) hasgood compatibility with other liquid crystal compounds, and has a largedielectric anisotropy (Δ∈) and refractive index anisotropy (Δn).

(Composition of the Present Invention)

In the present invention, the characteristic values of the liquidcrystal compositions were measured following the methods below. Themethods are mainly those described in EIAJ•ED-2521A of the Standard ofElectric Industries Association of Japan or modifications of the same.The TN device used in the measurement was not equipped with TFT.

Upper-limit temperature of a nematic phase (NI, ° C.): a sample wasplaced on a hot plate in a melting point measuring apparatus equippedwith a polarizing microscope, and heated at a rate of 1° C./min. Thetemperature at which a part of the sample began to change from a nematicphase into an isotropic liquid was recorded as the upper-limittemperature of the nematic phase, which is sometimes abbreviated as“upper-limit temperature”.

Lower-limit temperature of a nematic phase (T_(C), ° C.): a samplehaving a nematic phase was kept in a freezer at 0° C., −10° C., −20° C.,−30° C., and −40° C. for 10 days, and observed for the liquid crystalphase. For example, in a case where the sample exhibits a nematic phaseat −20° C., and is changed to a crystal or a smectic phase at −30° C.,the T_(C) is recorded as ≦−20° C. The lower-limit temperature of anematic phase is sometimes abbreviated as “lower-limit temperature”.

Transition temperature of an optically isotropic liquid crystal phase: asample was placed on a hot plate in a melting point measuring apparatusequipped with a polarizing microscope, and in a crossed nicols state,initially heated to a temperature allowing the sample to change into anon-liquid crystal isotropic phase, and then cooled at a rate of 1°C./min until a chiral nematic phase or an optically isotropic liquidcrystal phase was completely formed. The phase transition temperatureduring this cooling process was measured. Then, the temperature wasraised at a rate of 1° C./min, and the phase transition temperatureduring this heating process was measured. In the present invention,unless specifically indicated, the phase transition temperature in theheating process was recorded as the phase transition temperature. Whereit was difficult to determine the phase transition temperature of theoptically isotropic liquid crystal phase in a dark field under crossednicols, the phase transition temperature could be determined after thepolarizing plate is deviated from the crossed polarization state by 1-10degrees.

Viscosity (η, determined at 20° C., mPa·s): the viscosity was measuredwith an E-type rotational viscometer.

Rotational viscosity (γ1, determined at 25° C., mPa·s):

1) For a sample with a positive dielectric anisotropy: the measurementwas carried out following the method described in M. Imai et al.,Molecular Crystals and Liquid Crystals, Vol. 259, 37 (1995). The samplewas placed into a TN device with a twist angle of 0 degree and adistance (cell gap) of 5 μm between two glass substrates. The TN devicewas applied with a voltage in a range of 16 to 19.5 V stepwise by 0.5 V.After a period of 0.2 s without voltage application a voltageapplication was repeated with a rectangular wave (rectangular pulse of0.2 s), followed by a period of 2 s without voltage application. Thepeak current and the peak time of the transient current resulted fromthe application of the voltage were measured. Then, the value ofrotational viscosity was calculated according to the measurements andthe Equation (8) described on page 40 of the paper of M. Imai et al. Thedielectric anisotropy value required for this calculation was obtainedby using the device used in the measurement of the rotational viscosity,following the method for determining dielectric anisotropy below.

2) For a sample with a negative dielectric anisotropy: the measurementwas carried out following the method described in M. Imai et al.,Molecular Crystals and Liquid Crystals, Vol. 259, 37 (1995). The samplewas placed into a vertical alignment (VA) device with a distance (cellgap) of 20 μm between two glass substrates. The device was applied witha voltage in a range of 30 to 50 V stepwise by 1 V. After a period of0.2 s without voltage application, a voltage application was repeatedwith a rectangular wave (rectangular pulse of 0.2 s) followed by aperiod of 2 s without voltage application. The peak current and the peaktime of the transient current resulted from the application of thevoltage were measured. Then, the value of rotational viscosity wascalculated according to the measurements and the Equation (8) describedon page 40 of the paper of M. Imai et al. The dielectric anisotropyvalue required for this calculation was obtained by using the method fordetermining dielectric anisotropy below.

Refractive index anisotropy (Δn, determined at 25° C.): the measurementwas carried out by using light having a wavelength of 589 nm, with anAbbe refractometer having a polarizing plate mounted on the ocular lens.After the surface of the main prism was rubbed in a direction, thesample was dropped onto the main prism. The refractive index (n_(//))was determined when the polarizing direction was paralleled to therubbing direction, and the refractive index (n_(⊥)) was determined whenthe polarizing direction was perpendicular to the rubbing direction. Thevalue of refractive index anisotropy was calculated according theequation Δn=n_(//)−n_(⊥). When the sample was a composition, the processcould be used to determine the refractive index anisotropy. When thesample was a compound, the compound was mixed with a suitablecomposition for determining the refractive index anisotropy. In thiscase, the refractive index anisotropy value of the compound was anextrapolated value.

Dielectric anisotropy (Δ∈, determined at 25° C.): when the sample was acompound, the compound was mixed with a suitable composition fordetermining the dielectric anisotropy. In this case, the dielectricanisotropy value of the compound was an extrapolated value.

1) For a composition with a positive dielectric anisotropy: a sample wasplaced into a liquid crystal cell with a distance (gap) of about 9 μmbetween two glass substrates and a twist angle of 80 degrees. The liquidcrystal cell was applied with a voltage of 20 V to determine thedielectric constant (∈_(//)) in the major axis direction of the liquidcrystal molecule. Then, a voltage of 0.5 V was applied to determine thedielectric constant (∈_(⊥)) in the minor axis direction of the liquidcrystal molecule. The value of dielectric anisotropy was calculatedaccording to the equation Δ∈=∈_(//)−∈_(⊥).

2) For a composition with a negative dielectric anisotropy: a sample wasplaced into a liquid crystal cell which was processed into a homeotropicalignment, and a voltage of 0.5 v was applied to determine thedielectric constant (∈_(//)). Then, the sample was placed into a liquidcrystal cell which was processed into a homogeneous alignment, and avoltage of 0.5 v was applied to determine the dielectric constant(∈_(⊥)). The value of dielectric anisotropy was calculated according tothe equation Δ∈=∈_(//)−∈_(⊥).

Threshold voltage (Vth, determined at 25° C., V): when the sample was acompound, the compound was mixed with a suitable composition fordetermining the threshold voltage. In this case, the threshold voltagevalue of the compound was an extrapolated value. 1) For a compositionwith a positive dielectric anisotropy: a sample was placed into an LCDdevice of a normally white mode with a distance (gap) of (0.5/Δn) μmbetween two glass substrates and a twist angle of 80 degrees, in whichΔn was the value of refractive index anisotropy determined by using themethod above. A rectangular wave with a frequency of 32 Hz was appliedto the device. Then, the voltage of the rectangular wave was increased,and the voltage value at which the transmittance of light through thedevice reached 90% was determined.

2) For a composition with a negative dielectric anisotropy: a sample wasplaced into an LCD device of a normally black mode with a distance (gap)of about 9 μm between two glass substrates, which was processed into ahomeotropic alignment. A rectangular wave with a frequency of 32 Hz wasapplied to the device. Then, the voltage of the rectangular wave wasincreased, and the voltage value at which the transmittance of lightthrough the device reached 10% was determined.

Voltage holding ratio (VHR, determined at 25° C., %): the TN device usedfor the determination had a polyimide alignment film and a distance(cell gap) of 6 μm between two glass substrates. A sample was placedinto the device, which was then sealed with a UV-polymerizable adhesive.Then, the TN device was charged by applying a pulse voltage (5V, 60 ms).The voltage decay was determined by using a high-speed voltmeter at aninterval of 16.7 ms, and the area A between the voltage curve and thehorizontal axis per unit cycle was calculated. The area B was an areawhere no decay occurs. The voltage holding ratio was the percentage ofthe area A relative to the area B.

Helical pitch (determined at 20° C., μm): The helical pitch was measuredaccording to the wedge cell method of Grandjean-Cano. A sample wasinjected into a wedge cell of Grandjean-Cano, and then the distance (a,in μm) between the disclination lines observed from the wedge cell wasmeasured. The helical pitch (p) could be calculated according to theequation p=2·a·tan θ, in which θ is the angle between the two glassplates in the wedge cell.

Alternatively, the pitch length can be determined with selectivereflection (Handbook of Liquid Crystal, p 196, issued in 2000, byMaruzen). For the selective reflection wavelength λ, the relationship<n>p/λ=1 exists, where <n> denotes the average refractive index, and canbe calculated with the equation <n>={(n_(//) ²+n_(⊥) ²)/2}^(1/2). Theselective reflection wavelength was determined with amicrospectrophotometer (trade name MSV-350, manufactured by JapanElectronics Co., Ltd). The pitch was obtained by dividing the resultingreflection wavelength by the average refractive index.

When the concentration of the chiral reagent is low, the pitch of thecholesteric liquid crystal having a reflection wavelength in a region ofwavelength longer than that of visible light is proportional to thereciprocal of the concentration. Therefore, multiple points weremeasured for the helical pitch length of the liquid crystal having aselective reflection wavelength in the visible light region, and thehelical pitch was calculated by using a linear extrapolation method.

The proportion (percentage) of a component or a liquid crystal compoundis weight percentage (wt %) based on the total weight of the liquidcrystal compounds. The composition can be prepared by mixing thecomponents including liquid crystal compounds after being weighed. Thus,the wt % of each component can be easily calculated.

Example 1

Liquid Crystal Composition A was prepared by mixing the liquid crystalcompounds shown below at the following ratios.

Corresponding general formulas are shown at the right sides of thestructural formulas.

Liquid Crystal Composition A

Then, Liquid Crystal Composition B containing Liquid Crystal CompositionA (94 wt %) and a chiral reagent ISO-60BA2 (6 wt %) of the formula belowwas obtained.

In addition, ISO-60BA2 was obtained by esterifying isosorbide and4-hexyloxybenzoic acid in the presence of dicyclohexyl Carbodiimide(DCC), and 4-dimethylpyridine.

Example 2

Preparation of Mixture of Monomer and Liquid Crystal Composition

As a mixture of a monomer and a liquid crystal composition, LiquidCrystal Composition C-M was prepared by mixing 79.4 wt % liquid crystalcomposition B, 10.0 wt % n-dodecyl acrylate, 10.0 wt %1,4-di(4-(6-(acryloxy)hexyloxy)benzoyloxy)-2-toluene, and 0.6 wt %2,2′-dimethoxybenzylacetophenone as a photo polymerization initiator.

Preparation of Polymer/Liquid Crystal Composite Material

Liquid Crystal Composition C-M was held between a non-aligned comb-likeelectrode substrate and a glass substrate (without electrode) oppositeto the comb-like electrode substrate with a cell thickness of 10 μm, andthen the resulting liquid crystal cell was heated to 63.0° C. In thisstate, the cell was irradiated with UV light of 365 nm at an intensityof 23 mWcm⁻² for 1 min for polymerization.

The polymer/liquid crystal composite material C-P thus prepared couldmaintain an optically isotropic liquid crystal phase even being cooledto room temperature.

Furthermore, as shown in FIG. 1, the electrodes on the comb-likeelectrode substrate have such a structure that Electrode 1 extendingfrom the left side and Electrode 2 extending from the right side arealternatively arranged. Thus, when a potential difference exists betweenElectrode 1 and Electrode 2, the comb-like electrode substrate can beprovided with an electric field in two directions (upward and downward),as shown in FIG. 1.

Example 3

A liquid crystal cell holding the polymer/liquid crystal compositematerial C-1P obtained in Example 2 was disposed in the optical systemof FIG. 2 to measure the electro-optic properties, as follows. Using thewhite light source of a polarizing microscope (ECLIPSE LV100POL,manufactured by Nikon) as a light source, the incident light from thewhite light source irradiated on the liquid crystal cell wasperpendicular to the liquid crystal cell plane, and the line directionof the comb-like electrode was at 45 degrees with respect to thepolarizer and the analyzer respectively. The relationship between theapplied voltage and the transmittance was investigated by setting themeasuring temperature at the clearing point (59.1° C.)−40° C. =19.1° C.If a rectangular wave of 47.6 V was applied, then the transmittance wasup to 80%, and the transmitted light intensity was saturated.

Example 4

Liquid Crystal Composition D was prepared by mixing the liquid crystalcompounds shown below at the following ratios.

Corresponding general formulas are shown at the right sides of thestructural formulas.

Liquid Crystal Composition D

Then, Liquid Crystal Composition E containing Liquid Crystal CompositionD (94 wt %) and a chiral reagent 2 (6.1 wt %) of the formula below wasobtained.

Structural Formula of Chiral Reagent 2

Example 5

Preparation of Mixture of Monomer and Liquid Crystal Composition

As a mixture of a monomer and a liquid crystal composition, LiquidCrystal Compositions F-M were prepared by mixing 87.4 wt % LiquidCrystal Composition E, 6.0 wt % n-dodecyl acrylate, 6.0 wt %1,4-di(4-(6-(acryloxy)propoxy)benzoyloxy)-2-toluene, and 0.6 wt %2,2′-dimethoxybenzylacetophenone as a photo polymerization initiator.

Preparation of Polymer/Liquid Crystal Composite Material

Liquid Crystal Compositions F-M were held between a non-alignedcomb-like electrode substrate and an glass substrate (without electrode)opposite to the comb-like electrode substrate with a cell thickness of10 μm, and then the resulting liquid crystal cell was heated to 77.0° C.In this state, the cell was irradiated with UV light of 365 nm at anintensity of 23 mWcm⁻² for 1 min for polymerization.

The polymer/liquid crystal composite material F-P thus prepared couldmaintain an optically isotropic liquid crystal phase even being cooledto room temperature.

Furthermore, as shown in FIG. 1, the electrodes on the comb-likeelectrode substrate have such a structure that Electrode 1 extendingfrom the left side and Electrode 2 extending from the right side arealternatively arranged. Thus, when a potential difference exists betweenElectrode 1 and Electrode 2, the comb-like electrode substrate can beprovided with an electric field in two directions (upward and downward),as shown in FIG. 1.

Example 6

A liquid crystal cell holding the polymer/liquid crystal compositematerial F-P obtained in Example 5 was disposed in the optical system ofFIG. 2 to measure the electro-optic properties, as follows. Using thewhite light source of a polarizing microscope (ECLIPSE LV100POL,manufactured by Nikon) as a light source, the incident light from thewhite light source irradiated on the liquid crystal cell wasperpendicular to the liquid crystal cell plane, and the line directionof the comb-like electrode was at 45 degrees with respect to thepolarizer and the analyzer respectively. The relationship between theapplied voltage and the transmittance was investigated by setting themeasuring temperature at the clearing point of Liquid CrystalComposition E (64.9° C.)−25° C.=39.9° C. If a rectangular wave of 58 Vwas applied, then the transmittance was up to 80%, and the transmittedlight intensity was saturated.

Example 7

Liquid Crystal Composition G was prepared by mixing Liquid CrystalComposition D and Liquid Crystal Compound (16-16a) below at a weightratio of 85/15.

Then, Liquid Crystal Composition H containing Liquid Crystal CompositionG (94 wt %) and the chiral reagent 2 (7.0 wt %) was obtained.

Example 8

Preparation of Mixture of Monomer and Liquid Crystal Composition

As a mixture of a monomer and a liquid crystal composition, LiquidCrystal Composition I-M was prepared by mixing 87.4 wt % Liquid CrystalComposition H, 6.0 wt % n-dodecyl acrylate, 6.0 wt %1,4-di(4-(6-(acryloxy)propoxy)benzoyloxy)-2-toluene, and 0.6 wt %2,2′-dimethoxybenzylacetophenone as a photo polymerization initiator.

Preparation of Polymer/Liquid Crystal Composite Material

Liquid Crystal Composition I-M was held between a non-aligned comb-likeelectrode substrate and an opposite glass substrate (without electrode)opposite to the comb-like electrode substrate with a cell thickness of10 μm, and then the resulting liquid crystal cell was heated to 60.0° C.In this state, the cell was irradiated with UV light of 365 nm at anintensity of 23 mWcm⁻² for 1 min for polymerization.

The polymer/liquid crystal composite material I-P thus prepared couldmaintain an optically isotropic liquid crystal phase even being cooledto room temperature.

Furthermore, as shown in FIG. 1, the electrodes on the comb-likeelectrode substrate have such a structure that Electrode 1 extendingfrom the left side and Electrode 2 extending from the right side arealternatively arranged. Thus, when a potential difference exists betweenElectrode 1 and Electrode 2, the comb-like electrode substrate can beprovided with an electric field in two directions (upward and downward),as shown in FIG. 1.

Example 9

A liquid crystal cell holding the polymer/liquid crystal compositematerial I-P obtained in Example 8 was disposed in the optical system ofFIG. 2 to measure the electro-optic properties, as follows. Using thewhite light source of a polarizing microscope (ECLIPSE LV100POL,manufactured by Nikon) as a light source, the incident light from thewhite light source irradiated on the liquid crystal cell wasperpendicular to the liquid crystal cell plane, and the line directionof the comb-like electrode was at 45 degrees with respect to thepolarizer and the analyzer respectively. The relationship between theapplied voltage and the transmittance was investigated by setting themeasuring temperature at the clearing point of Liquid CrystalComposition H (57.1° C.)−25° C.=32.1° C. If a rectangular wave of 58 Vwas applied, then the transmittance was up to 80%, and the transmittedlight intensity was saturated.

[Applicability in Industry]

The present invention is applicable, for example, in the field ofoptical devices, such as display devices using a liquid crystal medium.

What is claimed is:
 1. A liquid crystal composition, comprising anachiral component T comprising a compound of Formula (1) and a chiralreagent, and exhibiting an optically isotropic liquid crystal phase,

wherein in Formula (1), R¹ is hydrogen or a C₁₋₂₀ alkyl in whicharbitrary —CH₂— may be substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—,—CF═CF— or —C≡C—, and arbitrary hydrogen in the alkyl and the alkyl witharbitrary —CH₂— substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—,—CF═CF—, or —C≡C— may be substituted with halogen or a C₁₋₃ alkyl; Z¹,Z², and Z³ are each independently a single bond, —COO—, or —CF₂O—,provided that at least one of Z¹, Z², and Z³ is —CF₂O—; and L¹, L², L³,L⁴, and L⁵ are each independently hydrogen or fluorine; X¹ is hydrogen,halogen, —SF₅, or a C₁₋₁₀ alkyl in which arbitrary —CH₂— may besubstituted with —O—, —S—, —CH═CH—, or —C≡C—, and arbitrary hydrogen inthe alkyl and the alkyl with arbitrary —CH₂— substituted with —O—, —S—,—CH═CH—, or —C≡C— may be substituted with fluorine.
 2. The liquidcrystal composition according to claim 1, wherein in Formula (1), R¹ isa C₁₋₂₀ alkyl, a C₂₋₂₁ alkenyl, a C₂₋₂₁ alkynyl, a C₁₋₁₉ alkoxy, a C₂₋₂₀alkenyloxy, a C₁₋₁₉ alkylthio, a C₁₋₁₉ alkenylthio, or —(CH₂)v-CH═CF₂,in which v is an integer of 0 or 1-19; and X¹ is hydrogen, halogen,—SF₅, —CH₂F, —CHF₂, —CF₃, —(CH₂)₂—F, —CF₂CH₂F, —CF₂CHF₂, —CH₂CF₃,—CF₂CF₃, —(CH₂)₃—F, —(CF₂)₃—F, —CF₂CHFCF₃, —CHFCF₂CF₃, —(CH₂)₄—F,—(CF₂)₄—F, —(CH₂)₅—F, —(CF₂)₅—F, —OCH₂F, —OCHF₂, —OCF₃, —O—(CH₂)₂-—,—OCF₂CH₂F, —OCF₂CHF₂, —OCH₂CF₃, —O—(CH₂)₃—F, —O—(CF₂)₃—F, —OCF₂CHFCF₃,—OCHFCF₂CF₃, —O—(CH₂)₄—F, —O—(CF₂)₄—F, —O—(CH₂)₅—F, —O—(CF₂)₅—F,—CH═CHF, —CH═CF₂, —CF═CHF, —CH═CHCH₂F, —CH═CHCF₃, —(CH₂)₂—CH═CF₂,—CH₂CH═CHCF₃, or —CH═CHCF₂CF₃.
 3. The liquid crystal compositionaccording to claim 1, wherein in Formula (1), Z¹, Z², and Z³ are eachindependently a single bond or —CF₂O—.
 4. The liquid crystal compositionaccording to claim 1, wherein R¹ is a group of any one of Formulas(CHN-1)—(CHN-19), and R^(1a) is hydrogen or a C₁₋₂₀ alkyl,


5. The liquid crystal composition according to claim 1, comprising atleast one compound selected from the group consisting of the compoundsof Formulas (1-1)-(1-3):

wherein in the formulas, R¹ is a group of any one of Formulas(CHN-1)-(CHN-19), and R^(1a) is hydrogen or a C₁₋₂₀ alkyl; L¹, L², L³,L⁴, and L⁵ are each independently hydrogen or fluorine; and X¹ isfluorine, chlorine, —CF₃, —CHF₂, —CH₂F, —OCF₃, —OCHF₂, —OCH₂F,—OCF₂CFHCF₃, or —CH═CHCF₃,


6. The liquid crystal composition according to claim 5, wherein inFormulas (1-1)-(1-3), R¹ is a group of any one of Formulas(CHN-1)-(CHN-4) and Formulas (CHN-6)-(CHN-8), and R^(1a) is hydrogen ora C₁₋₂₀ alkyl,


7. The liquid crystal composition according to claim 1, wherein theachiral component T further comprises a compound of Formula (2):

wherein in Formula (2), R² is hydrogen or a C₁₋₂₀ alkyl in whicharbitrary —CH₂— may be substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—,—CF═CF— or —C≡C—, and arbitrary hydrogen in the alkyl and the alkyl witharbitrary —CH₂— substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—,—CF═CF— or —C≡C— may be substituted with halogen or a C₁₋₃ alkyl; RingsA¹, A², A³, A⁴, and A⁵ are each independently a benzene ring, anaphthalene ring, a thiophene ring, a piperidine ring, a cyclohexenering, a bicyclooctane ring, a tetrahydronaphthalene ring or acyclohexane ring, wherein arbitrary hydrogen in the rings may besubstituted with halogen, a C₁₋₃ alkyl, a C₁₋₃ alkoxy, or a C₁₋₃haloalkyl, —CH₂— in the rings may be substituted with —O— or —S—, and—CH═ in the rings may be substituted with —N═; Z⁴, Z⁵, Z⁶, Z⁷, Z⁸, andZ⁹ are each independently a single bond or a C₁₋₄ alkylene in whicharbitrary —CH₂— may be substituted with —O—, —S—, —COO—, —OCO—, —CSO—,—OCS—, —CH═CH—, —CF═CF— C≡C—, and arbitrary hydrogen in the alkylene orthe alkylene with arbitrary —CH₂— substituted with —O—, —S—, —COO—,—OCO—, —CSO—, —OCS—, —CH═CH—, —CF═CF— or —C≡C— may be substituted withhalogen; L⁶, L⁷, and L⁸ are each independently hydrogen or halogen; X²is hydrogen, halogen, —C≡N, —N═C═S, —C≡C—C≡N, —SF₅, or a C₁₋₁₀ alkyl inwhich arbitrary —CH₂— may be substituted with —O—, —S—, —CH═CH— or—C≡C—, and arbitrary hydrogen in the alkyl and the alkyl with arbitrary—CH₂— substituted with —O—, —S—, —CH═CH— or —C≡C— may be substitutedwith halogen; and l, m, n, o and p are each independently 0 or 1,provided that l+m+n+o+p≦4.
 8. The liquid crystal composition accordingto claim 7, wherein in Formula (2), R² is a group of any one of Formulas(CHN-1)-(CHN-4) and Formulas (CHN-6)-(CHN-7), R^(1a) is hydrogen or aC₁₋₂₀ alkyl; Rings A¹, A², A³, A⁴, and A⁵ are (RG-1)-(RG-13); Z⁴, Z⁵,Z⁶, Z⁷, Z⁸, and Z⁹ are each independently a single bond or a C₁₋₄alkylene in which arbitrary —CH₂— may be substituted with —O—, —COO— or—CF₂O—; L⁶, L⁷ and L⁸ are each independently hydrogen or fluorine; X² isfluorine, chlorine, —CF₃, —CHF₂, —CH₂F, —OCF₃, —OCHF₂, —OCH₂F,—OCF₂CFHCF₃, or —CH═CHCF₃; and l, m, n, o, and p are each independently0 or 1, provided that l+m+n+o+p≦4,


9. The liquid crystal composition according to claim 8, wherein in thecompound of Formula (2), 2≦l+m+n+o+p≦3.
 10. The liquid crystalcomposition according to claim 1, wherein the achiral component Tcomprises only the compound of Formula (1).
 11. The liquid crystalcomposition according to claim 7, wherein the achiral component Tcomprises only 5-95 weight percent (wt %) of the compound of Formula (1)and 5-50 wt % of the compound of Formula (2).
 12. The liquid crystalcomposition according to claim 7, wherein the achiral component Tcomprises 5-95 wt % of the compound of Formula (1), 5-80 wt % of thecompound of Formula (2), and 0-50 wt % of other compounds.
 13. Theliquid crystal composition according to claim 7, wherein the achiralcomponent T comprises 5-94 wt % of the compound of Formula (1), 5-80 wt% of the compound of Formula (2), and 1-50 wt % of other compounds. 14.The liquid crystal composition according to claim 1, wherein the achiralcomponent T comprises 10-100 wt % of a compound selected from the groupconsisting of Formulas (1-2A)-(1-2H) and Formulas (1-3A)-(1-3D):

wherein in the formulas, R¹ is a chain selected from Formulas (CHN-1),(CHN-4), (CHN-7), (CHN-8) and (CHN-11); and X¹ is fluorine, chlorine,—CF₃, —CHF₂, —CH₂F, —OCF₃, —OCHF₂, —OCF₂CFHCF₃, or —CH═CHCF₃.
 15. Theliquid crystal composition according to claim 1, wherein the achiralcomponent T further comprises at least one compound selected from thegroup consisting of the compounds of Formulas (3), (4), and (5):

wherein in the formulas, R³ is a C₁₋₁₀ alkyl or a C₂₋₁₀ alkenyl, whereinarbitrary hydrogen in the alkyl and the alkenyl may be substituted withfluorine, and arbitrary —CH₂— in the alkyl, the alkenyl, or the alkyland the alkenyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X³ is fluorine, chlorine, —OCF₃, —OCHF₂, —CF₃,—CHF₂, —CH₂F, —OCF₂CHF₂, or —OCF₂CHFCF₃; Rings B¹, B², and B³ are eachindependently 1,4-cyclohexylene, 1,3-dioxane-2,5-diyl,pyrimidine-2,5-diyl, tetrahydropyran-2,5-diyl, 1,4-phenylene,naphthalene-2,6-diyl, 1,4-phenylene with arbitrary hydrogen substitutedwith fluorine, or naphthalene-2,6-diyl with arbitrary hydrogensubstituted with fluorine or chlorine; in Formula (5), Ring B1 is1,4-cyclohexylene, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl,tetrahydropyran-2,5-diyl, 1,4-phenylene, naphthalene-2,6-diyl, ornaphthalene-2,6-diyl with arbitrary hydrogen substituted with fluorineor chlorine; Z¹⁰ and Z¹¹ are each independently —(CH₂)₂—, —(CH₂)₄—,—COO—, —CF₂O—, —OCF₂—, —CH═CH—, —C≡C—, —CH₂O—, or a single bond; and L⁹and L¹⁰ are each independently hydrogen or fluorine.
 16. The liquidcrystal composition according to claim 1, wherein the achiral componentT further comprises at least one compound selected from the groupconsisting of the compound of Formula (6):

wherein in the formula, R⁴ is a C₁₋₁₀ alkyl or a C₂₋₁₀ alkenyl, whereinarbitrary hydrogen in the alkyl and the alkenyl may be substituted withfluorine, and arbitrary —CH₂— in the alkyl, the alkenyl, or the alkyland the alkenyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X⁴ is —C≡N or —C≡C—C≡N; Rings C¹, C², and C³ areeach independently 1,4-cyclohexylene, 1,4-phenylene, 1,4-phenylene witharbitrary hydrogen substituted with fluorine, naphthalene-2,6-diyl,naphthalene-2,6-diyl with arbitrary hydrogen substituted with fluorineor chlorine, 1,3-dioxane-2,5-diyl, tetrahydropyran-2,5-diyl, orpyrimidine-2,5-diyl; Z¹² is —(CH₂)₂—, —COO—, —CF₂O—, —OCF₂—, —C≡C—,—CH₂O—, or a single bond; L¹¹ and L¹² are each independently hydrogen orfluorine; and r is 0, 1, or 2, s is 0 or 1, and r+s=0, 1 or
 2. 17. Theliquid crystal composition according to claim 1, wherein the achiralcomponent T further comprises at least one compound selected from thegroup consisting of Formulas (7), (8), (9), (10), and (11):

wherein in the formulas, R⁵ and R⁶ are each independently a C₁₋₁₀ alkylor a C₂₋₁₀ alkenyl, wherein arbitrary hydrogen in the alkyl and thealkenyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, or the alkyl and the alkenyl with arbitrary hydrogensubstituted with fluorine may be substituted with —O—; Rings D¹, D², D³,and D⁴ are each independently 1,4-cyclohexylene, 1,4-cyclohexenylene,1,4-phenylene, 1,4-phenylene with arbitrary hydrogen substituted withfluorine, tetrahydropyran-2,5-diyl, or decahydronaphthalene-2,6-diyl;Z¹³, Z¹⁴, Z¹⁵, and Z¹⁶ are each independently —(CH₂)₂—, —COO—, —CH₂O—,—OCF₂—, —OCF₂(CH₂)₂—, or a single bond; L¹³ and L¹⁴ are eachindependently fluorine or chlorine; and t, u, x, y, and z are eachindependently 0 or 1, and u+x+y+z is 1 or
 2. 18. The liquid crystalcomposition according to claim 1, wherein the achiral component Tfurther comprises at least one compound selected from the groupconsisting of the compounds of Formulas (12), (13), and (14):

wherein in the formulas, R⁷ and R⁸ are each independently a C₁₋₁₀ alkylor a C₂₋₁₀ alkenyl, in which arbitrary hydrogen in the alkyl and thealkenyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, or the alkyl and the alkenyl with arbitrary hydrogensubstituted with fluorine may be substituted with —O—; Rings E¹, E², andE³ are each independently 1,4-cyclohexylene, pyrimidine-2,5-diyl,1,4-phenylene, 2-fluoro-1,4-phenylene, 3-fluoro-1,4-phenylene, or2,5-difluoro-1,4-phenylene; Z¹⁷ and Z¹⁸ are each independently —C≡C—,—COO—, —(CH₂)₂—, —CH═CH—, or a single bond.
 19. The liquid crystalcomposition according to claim 15, further comprising at least onecompound selected from the group consisting of the compound of Formula(6):

wherein in the formula, R⁴ is a C₁₋₁₀ alkyl or a C₂₋₁₀ alkenyl, whereinarbitrary hydrogen in the alkyl and the alkenyl may be substituted withfluorine, and arbitrary —CH₂— in the alkyl, the alkenyl, or the alkyland the alkenyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X⁴ is —C≡N or —C≡C—C≡N; Rings C¹, C², and C³ areeach independently 1,4-cyclohexylene, 1,4-phenylene, 1,4-phenylene witharbitrary hydrogen substituted with fluorine, naphthalene-2,6-diyl,naphthalene-2,6-diyl with arbitrary hydrogen substituted with fluorineor chlorine, 1,3-dioxane-2,5-diyl, tetrahydropyran-2,5-diyl, orpyrimidine-2,5-diyl; Z¹² is —(CH₂)₂—, —COO—, —CF₂O—, —OCF₂—, —CH≡C—,—CH₂O—, or a single bond; L¹¹ and L¹² are each independently hydrogen orfluorine; and r is 0, 1, or 2, s is 0 or 1, and r+s=0, 1 or
 2. 20. Theliquid crystal composition according to claim 15, further comprising atleast one compound selected from the group consisting of the compoundsof Formula (12), (13), and (14):

wherein in the formulas, R⁷ and R⁸ are each independently a C₁₋₁₀ alkylor a C₂₋₁₀ alkenyl, in which arbitrary hydrogen in the alkyl and thealkenyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, or the alkyl and the alkenyl with arbitrary hydrogensubstituted with fluorine may be substituted with —O—; Rings E¹, E², andE³ are each independently 1,4-cyclohexylene, pyrimidine-2,5-diyl,1,4-phenylene, 2-fluoro-1,4-phenylene, 3-fluoro-1,4-phenylene, or2,5-difluoro-1,4-phenylene; Z¹⁷ and Z¹⁸ are each independently —C≡C—,—COO—, —(CH₂)₂—, —CH═CH—, or a single bond.
 21. The liquid crystalcomposition according to claim 16, further comprising at least onecompound selected from the group consisting of the compounds of Formulas(12), (13), and (14):

wherein in the formulas, R⁷ and R⁸ are each independently a C₁₋₁₀ alkylor a C₂₋₁₀ alkenyl, in which arbitrary hydrogen in the alkyl and thealkenyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, or the alkyl and the alkenyl with arbitrary hydrogensubstituted with fluorine may be substituted with —O—; Rings E¹, E², andE³ are each independently 1,4-cyclohexylene, pyrimidine-2,5-diyl,1,4-phenylene, 2-fluoro-1,4-phenylene, 3-fluoro-1,4-phenylene, or2,5-difluoro-1,4-phenylene; Z¹⁷ and Z¹⁸ are each independently —C≡C—,—COO—, —(CH₂)₂—, —CH═CH—, or a single bond.
 22. The liquid crystalcomposition according to claim 17, further comprising at least onecompound selected from the group consisting of the compounds of Formulas(1), (13), and (14):

wherein in the formulas, R⁷ and R⁸ are each independently a C₁₋₁₀ alkylor a C₂₋₁₀ alkenyl, in which arbitrary hydrogen in the alkyl and thealkenyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, or the alkyl and the alkenyl with arbitrary hydrogensubstituted with fluorine may be substituted with —O—; Rings E¹, E², andE³ are each independently 1,4-cyclohexylene, pyrimidine-2,5-diyl,1,4-phenylene, 2-fluoro-1,4-phenylene, 3-fluoro-1,4-phenylene, or2,5-difluoro-1,4-phenylene; Z¹⁷ and Z¹⁸ are each independently —C≡C—,—COO—, —(CH₂)₂—, —CH═CH—, or a single bond.
 23. The liquid crystalcomposition according to claim 1, wherein the achiral component Tfurther comprises at least one compound selected from the groupconsisting of the compound of Formulas (15), (16), (17), and (18):

wherein in the formulas, R⁹ is a C₁₋₁₀ alkyl, a C₂₋₁₀ alkenyl, or aC₂₋₁₀ alkynyl, wherein arbitrary hydrogen in the alkyl, the alkenyl andthe alkynyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, the alkynyl, or the alkyl, the alkenyl and thealkynyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X⁵ is fluorine, chlorine, —SF₅, —OCF₃, —OCHF₂,—CF₃, —CHF₂, —CH₂F, —OCF₂CHF₂, or —OCF₂CHFCF₃; Rings F¹, F², F³, and F⁴are each independently 1,4-cyclohexylene, 1,3-dioxane-2,5-diyl,pyrimidine-2,5-diyl, tetrahydropyran-2,5-diyl, 1,4-phenylene,naphthalene-2,6-diyl, 1,4-phenylene with arbitrary hydrogen substitutedwith fluorine or chlorine, or naphthalene-2,6-diyl with arbitraryhydrogen substituted with fluorine or chlorine; in Formulas (17), RingF¹ is 1,4-cyclohexylene, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl,tetrahydropyran-2,5-diyl, 1,4-phenylene, naphthalene-2,6-diyl, ornaphthalene-2,6-diyl with arbitrary hydrogen substituted with fluorineor chlorine; Z¹⁹, Z²⁰, and Z²¹ are each independently —(CH₂)₂—,—(CH₂)₄—, —COO—, —CF₂O—, —OCF₂—, —CH═CH—, —CH≡C—, —CH₂O—, or a singlebond; and L¹⁵ and L¹⁶ are each independently hydrogen or fluorine. 24.The liquid crystal composition according to claim 1, wherein the achiralcomponent T further comprises at least one compound selected from thegroup consisting of the compound of Formula (19):

wherein in the formulas, R¹⁰ is a C₁₋₁₀ alkyl, a C₂₋₁₀ alkenyl, or aC₂₋₁₀ alkynyl, wherein arbitrary hydrogen in the alkyl, the alkenyl andthe alkynyl may be substituted with fluorine, and arbitrary —CH₂— in thealkyl, the alkenyl, the alkynyl, or the alkyl, the alkenyl and thealkynyl with arbitrary hydrogen substituted with fluorine may besubstituted with —O—; X⁶ is —C≡N, —N═C═S, or —C≡C—C≡N; Rings G¹, G², andG³ are each independently 1,4-cyclohexylene, 1,4-phenylene,1,4-phenylene with arbitrary hydrogen substituted with fluorine orchlorine, naphthalene-2,6-diyl, naphthalene-2,6-diyl with arbitraryhydrogen substituted with fluorine or chlorine, 1,3-dioxane-2,5-diyl,tetrahydropyran-2,5-diyl, or pyrimidine-2,5-diyl; Z²² is —(CH₂)₂—,—COO—, —CF₂O—, —OCF₂—, —CH₂O—, or a single bond; L¹⁷ and L¹⁸ are eachindependently hydrogen or fluorine; and aa is 0, 1 or 2, ab is 0 or 1,and aa+ab is 0, 1 or
 2. 25. The liquid crystal composition according toclaim 1, comprising at least one antioxidant and/or UV absorbent. 26.The liquid crystal composition according to claim 1, wherein theoptically isotropic liquid crystal phase does not exhibit two or morecolors of diffracted light.
 27. The liquid crystal composition accordingto claim 1, wherein the optically isotropic liquid crystal phaseexhibits two or more colors of diffracted light.
 28. The liquid crystalcomposition according to claim 26, obtained by adding the chiral reagentinto a composition having a temperature difference of 3° C.-150° C.between an upper-limit temperature and a lower-limit temperature ofco-existence of a chiral nematic phase and a non-liquid crystalisotropic phase.
 29. The liquid crystal composition according to claim26, obtained by adding the chiral reagent into a composition having atemperature difference of 5° C.-150° C. between an upper-limittemperature and a lower-limit temperature of co-existence of a chiralnematic phase and a non-liquid crystal isotropic phase.
 30. The liquidcrystal composition according to claim 26, obtained by adding the chiralreagent into a composition having a temperature difference of 3° C.-150°C. between an upper-limit temperature and a lower-limit temperature ofco-existence of a nematic phase and a non-liquid crystal isotropicphase.
 31. The liquid crystal composition according to claim 1, whereina content of the chiral reagent is 1-40 wt % based on the total weightof the liquid crystal composition.
 32. The liquid crystal compositionaccording to claim 1, wherein a content of the chiral reagent is 5-15 wt% based on the total weight of the liquid crystal composition.
 33. Theliquid crystal composition according to claim 31, exhibiting a chiralnematic phase at any temperature in the range of 70° C. to −20° C., andhaving a helical pitch of 700 nm or less within at least a part of thetemperature range.
 34. The liquid crystal composition according to claim31, wherein the chiral reagent comprises at least one compound selectedfrom the group consisting of the compounds of Formulas (K1)-(K5):

wherein in Formulas (K1)-(K5), R^(K) is each independently hydrogen,halogen, —C≡N, —N═C═O, —N═C═S, or a C₁₋₂₀ alkyl in which arbitrary —CH₂—may be substituted substituted with —O—, —S—, —COO—, —OCO—, —CH═CH—,—CF═CF— or —C≡C—, arbitrary hydrogen in the alkyl may be substitutedwith halogen, and additionally, a terminal —CH₃ may be substituted with:

A is each independently an aromatic or non-aromatic 3- to 8-memberedring, or a fused ring having 9 or more carbon atoms, wherein arbitraryhydrogen in the rings may be substituted with halogen, a C₁₋₃ alkyl orhaloalkyl, —CH₂— in the rings may be substituted with —O—, —S—, or —NH—,and —CH═ in the rings may be substituted with —N═; B is eachindependently hydrogen, halogen, a C₁₋₃ alkyl, a C₁₋₃ haloalkyl, anaromatic or non-aromatic 3- to 8-membered ring, or a fused ring having 9or more carbon atoms, wherein arbitrary hydrogen in the rings may besubstituted with halogen, a C₁₋₃ alkyl or haloalkyl, —CH₂— in the ringsmay be substituted with —O—, —S—or —NH—, and —CH═ in the rings may besubstituted with —N═; Z is each independently a single bond, or a C₁₋₈alkylene in which arbitrary —CH₂— may be substituted with —O—, —S—,—COO—, —OCO—, —CSO—, —OCS—, —N═N—, —CH═N—, —N═CH—, —CH═CH—, —CF═CF—, or—C≡C—, and arbitrary hydrogen in the alkylene may be substituted withhalogen; X is a single bond, —COO—, —OCO—, —CH₂O—, —OCH₂—, —CF₂O—,—OCF₂—, or —CH₂CH₂—; and mK is an integer of 1-4.
 35. The liquid crystalcomposition according to claim 31, wherein the chiral reagent comprisesat least one compound selected from the group consisting of thecompounds of Formulas (K2-1)-(K2-8), Formulas (K4-1)-(K4-6), andFormulas (K5-1)-(K5-3):

wherein in the formulas, R^(K) is each independently a C₃₋₁₀ alkyl,wherein —CH₂— adjacent to a ring in the alkyl may be substituted with—O—, and arbitrary —CH₂— in the alkyl may be substituted with —CH═CH—.36. A mixture, comprising the liquid crystal composition according toclaim 1 and a polymerizable monomer.
 37. The mixture according to claim36, wherein the polymerizable monomer is a photopolymerizable monomer ora thermal-polymerizable monomer.
 38. A polymer/liquid crystal compositematerial, obtained by polymerizing the mixture comprising the liquidcrystal composition according to claim 1 and a polymerizable monomer,for use in a device driven in an optically isotropic liquid crystalphase.
 39. A polymer/liquid crystal composite material, obtained bypolymerizing the mixture comprising the liquid crystal compositionaccording to claim 1 and a polymerizable monomer in a non-liquid crystalisotropic phase or an optically isotropic liquid crystal phase.
 40. Thepolymer/liquid crystal composite material according to claim 38, whereinthe polymer in the polymer/liquid crystal composite material has amesogen moiety.
 41. The polymer/liquid crystal composite materialaccording to claim 38, wherein the polymer in the polymer/liquid crystalcomposite material has a cross-linked structure.
 42. The polymer/liquidcrystal composite material according to claim 38, wherein a content ofthe liquid crystal composition is 60-99 wt %, and a content of thepolymer is 1-40 wt %.
 43. An optical device, comprising a liquid crystalmedium disposed between substrates having electrodes disposed on eitheror both surfaces thereof and an electric field-applying means forapplying an electric field to the liquid crystal medium via theelectrodes, wherein the liquid crystal medium is the liquid crystalcomposition according to claim 1, wherein a content of the chiralreagent is 1-40 wt % based on the total weight of the liquid crystalcomposition or a polymer/liquid crystal composite material obtained bypolymerizing the mixture comprising the liquid crystal compositionaccording to claim 1 and a polymerizable monomer, for use in a devicedriven in an optically isotropic liquid crystal phase.
 44. An opticaldevice, comprising a set of substrates having electrodes disposed oneither or both surfaces thereof, at least one of which beingtransparent, a liquid crystal medium disposed between the substrates, apolarizer disposed outside of the substrates, and an electricfield-applying means for applying an electric field to the liquidcrystal medium via the electrodes, wherein the liquid crystal medium isthe liquid crystal composition according to claim 1, wherein a contentof the chiral reagent is 1-40 wt % based on the total weight of theliquid crystal composition or a polymer/liquid crystal compositematerial obtained by polymerizing the mixture comprising the liquidcrystal composition according to claim 1 and a polymerizable monomer,for use in a device driven in an optically isotropic liquid crystalphase.
 45. The optical device according to claim 43, wherein on at leastone of the set of substrates, the electrodes are configured in a mannersuch that an electric field is applied in at least two directions. 46.The optical device according to claim 43, wherein on one or two of theset of substrates disposed in parallel with each other, the electrodesare configured in a manner such that an electric field is applied in atleast two directions.
 47. The optical device according to claim 43,wherein the electrodes are disposed in a matrix form to form pixelelectrodes, and each pixel is provided with an active element being athin film transistor (TFT).